| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD，23℃ | ISO 294-4 | 0.60 到 0.80 | % |
| Modeling Shrinkage | MD2.0mm | ISO294-4 | 0.70 | % |
| Melt Volume flow Rate | 220℃/2.16 kg | ISO 1133 | 11.0 | cm3/10min |
| Melt Mass-Flow Rate | 220℃/10Kg | ISO1133 | 11.00 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 13 | kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 5.0 | kJ/m² |
| Charpy Notched Impact Strength | -30℃ | ISO 179 | 5.0 | kJ/m² |
| Tensile Stress | 23℃ | ISO 527-2 | 47.0 | Mpa |
| Tensile Modulus | 23°C | ISO527-2 | 2350 | Mpa |
| Tensile Modulus | 23℃ | ISO 527-2 | 2350 | Mpa |
| Tensile Strength | 23°C | ISO527-2 | 47 | Mpa |
| Rockwell Hardness | 23℃ | ISO 2039-2 | 107 | R 计秤 |
| Flexural Modulus | 23℃ | ISO 178 | 2600 | Mpa |
| Flexural Modulus | 23°C | ISO178 | 2600 | Mpa |
| Flexural Strength | 23°C | ISO178 | 76 | Mpa |
| Flexural Strength | 23℃ | ISO 178 | 76.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.80MPa，未退火 | ISO 75-2/Af | 82.0 | °C |
| Deflection Temperature Under Load? | 1.80MPa退火 | ISO75-2/Af | 82 | °C |
| Coefficient of Linear Thermal Expansion | MD | ISO11359-2 | 9E-05 | cm/cm/°C |
| Coefficient of Linear Thermal Expansion | 流动 | ISO 11359-2 | 0.000090 | cm/cm/℃ |
| Flame Rating | 1.50mm | UL 94 | HB | |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Insulation strength | | IEC60243-1 | 32 | KV/mm |
| Volume Resistivity | | IEC60093 | 1E+15 | Ω.cm |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | | ISO2039-2 | 107 | R |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Fire rating | | UL-94 | 1.50mm | HB |
| Fire rating | | UL-94 | 3.00mm | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.