Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD2.0mm | ISO294-4 | 0.70 | % |
Modeling Shrinkage | MD,23℃ | ISO 294-4 | 0.60 到 0.80 | % |
Melt Volume flow Rate | 220℃/2.16 kg | ISO 1133 | 11.0 | cm3/10min |
Melt Mass-Flow Rate | 220℃/10Kg | ISO1133 | 11.00 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Notched Impact Strength | -30℃ | ISO 179 | 5.0 | kJ/m² |
Charpy Notched Impact Strength | 23°C | ISO179/1eA | 13 | kJ/m² |
Charpy Notched Impact Strength | -30°C | ISO179/1eA | 5.0 | kJ/m² |
Tensile Stress | 23℃ | ISO 527-2 | 47.0 | Mpa |
Tensile Modulus | 23°C | ISO527-2 | 2350 | Mpa |
Tensile Modulus | 23℃ | ISO 527-2 | 2350 | Mpa |
Tensile Strength | 23°C | ISO527-2 | 47 | Mpa |
Rockwell Hardness | 23℃ | ISO 2039-2 | 107 | R 计秤 |
Flexural Modulus | 23°C | ISO178 | 2600 | Mpa |
Flexural Modulus | 23℃ | ISO 178 | 2600 | Mpa |
Flexural Strength | 23℃ | ISO 178 | 76.0 | Mpa |
Flexural Strength | 23°C | ISO178 | 76 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.80MPa,Unannealed | ISO 75-2/Af | 82.0 | °C |
Deflection Temperature Under Load? | 1.80MPaAnnealed | ISO75-2/Af | 82 | °C |
Coefficient of Linear Thermal Expansion | MD | ISO11359-2 | 9E-05 | cm/cm/°C |
Coefficient of Linear Thermal Expansion | Flow | ISO 11359-2 | 0.000090 | cm/cm/℃ |
Flame Rating | 1.50mm | UL 94 | HB | |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Insulation strength | | IEC60243-1 | 32 | KV/mm |
Volume Resistivity | | IEC60093 | 1E+15 | Ω.cm |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | | ISO2039-2 | 107 | R |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Fire rating | | UL-94 | 1.50mm | HB |
Fire rating | | UL-94 | 3.00mm | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.