Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
AES SE20 UMG JAPAN
DIALAC®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical Properties
Test Condition
Test Method
Unit
AES/UMG JAPAN/SE20
Melt Volume flow Rate
220℃/2.16 kg
ISO 1133
cm3/10min
1
Melt Mass-Flow Rate
220℃/10Kg
ISO1133
cm3/10min
1
Modeling Shrinkage
MD2.0mm
ISO294-4
%
0
Modeling Shrinkage
MD，23℃
ISO 294-4
%
0
Mechanical Properties
Test Condition
Test Method
Unit
AES/UMG JAPAN/SE20
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
1
Charpy Notched Impact Strength
-30°C
ISO179/1eA
kJ/m²
5
Charpy Notched Impact Strength
-30℃
ISO 179
kJ/m²
5
Tensile Modulus
23℃
ISO 527-2
Mpa
2
Tensile Modulus
23°C
ISO527-2
Mpa
2
Tensile Strength
23°C
ISO527-2
Mpa
4
Tensile Stress
23℃
ISO 527-2
Mpa
4
Rockwell Hardness
23℃
ISO 2039-2
R 计秤
1
Flexural Modulus
23°C
ISO178
Mpa
2
Flexural Modulus
23℃
ISO 178
Mpa
2
Flexural Strength
23℃
ISO 178
Mpa
7
Flexural Strength
23°C
ISO178
Mpa
7
Thermal Properties
Test Condition
Test Method
Unit
AES/UMG JAPAN/SE20
Deflection Temperature Under Load?
1.80MPa，未退火
ISO 75-2/Af
°C
8
Deflection Temperature Under Load?
1.80MPa退火
ISO75-2/Af
°C
8
Coefficient of Linear Thermal Expansion
MD
ISO11359-2
cm/cm/°C
9
Coefficient of Linear Thermal Expansion
流动
ISO 11359-2
cm/cm/℃
0
Electrical performance
Test Condition
Test Method
Unit
AES/UMG JAPAN/SE20
Insulation strength
IEC60243-1
KV/mm
3
Volume Resistivity
IEC60093
Ω.cm
1
hardness
Test Condition
Test Method
Unit
AES/UMG JAPAN/SE20
Rockwell Hardness
ISO2039-2
R
1
Flammability
Test Condition
Test Method
Unit
AES/UMG JAPAN/SE20
Fire rating
UL-94
HB
1
Fire rating
UL-94
HB
3