Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD:3.18mm | ASTMD955 | 0.0到0.20 | % |
| Modeling Shrinkage | TD:3.18mm | ASTMD955 | 1.5到1.7 | % |
| Moisture Absorption | 24hr | ASTMD570 | 0.10 | % |
| Melt Mass-Flow Rate | 400°C/2.16kg | ASTMD1238 | 1.1 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | 屈服 | ISO527-2/1A/5 | 217 | Mpa |
| Tensile Stress | -- | ASTMD638 | 201 | Mpa |
| Tensile Modulus | --4 | ASTMD638 | 19700 | Mpa |
| Tensile Modulus | -- | ISO527-2/1A/1 | 22800 | Mpa |
| Tensile Elongation | 断裂4 | ASTMD638 | 2.0 | % |
| Tensile Elongation | 断裂 | ISO527-2/1A/5 | 2.0 | % |
| Flexural Modulus | -- | ASTMD790 | 17500 | Mpa |
| Flexural Modulus | -- | ISO178 | 20500 | Mpa |
| Flexural Strength | -- | ASTMD790 | 317 | Mpa |
| Flexural Strength | -- | ISO178 | 311 | Mpa |
| Compressive Strength | | ASTMD695 | 173 | Mpa |
| Shearing Strength | | ASTMD732 | 95.1 | Mpa |
| Poisson Ratio | | 7.58 | 0.42 | |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Specific Heat | 50°C | DSC | 1130 | J/kg/°C |
| Specific Heat | 200°C | DSC | 1620 | J/kg/°C |
| Thermal Conductivity | | ASTME1530 | 0.37 | W/m/K |
| Deflection Temperature Under Load? | 1.8MPa,退火 | ASTMD648 | 315 | °C |
| Linear thermal expansion coefficient | MD：-50到50°C | ASTME831 | 5.2E-06 | cm/cm/°C |
| Peak Melting Temperature | | ASTMD3418 | 340 | °C |
| Glass Transition Temperature | | ASTMD3418 | 150 | °C |
| Fill Analysis | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Viscosity | 400°C,1000sec^-1 | ASTMD3835 | 920 | Pa·s |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Unnotched Izod Impact Strength | -- | ASTMD4812 | 750 | J/m |
| Unnotched Izod Impact Strength | -- | ISO180 | 44 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | M级 | ASTMD785 | 105 | |
| Shore Hardness | 邵氏D,1秒 | ASTMD2240 | 92 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.6mm | UL94 | V-0 | |
| UL flame retardant rating | 0.8mm | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare