Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEEK KT-820CF30 SOLVAY USA
KetaSpire® PEEK
Solvay、Solvie, Belgium
Filler: Carbon fiber rein、30% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical Properties
Test Condition
Test Method
Unit
PEEK/SOLVAY USA/KT-820CF30
Melt Mass-Flow Rate
400°C/2.16kg
ASTMD1238
g/10min
1
Modeling Shrinkage
MD:3.18mm
ASTMD955
%
0
Modeling Shrinkage
TD:3.18mm
ASTMD955
%
1
Moisture Absorption
24hr
ASTMD570
%
0
Mechanical Properties
Test Condition
Test Method
Unit
PEEK/SOLVAY USA/KT-820CF30
Shearing Strength
ASTMD732
Mpa
9
Tensile Modulus
--4
ASTMD638
Mpa
1
Tensile Modulus
--
ISO527-2/1A/1
Mpa
2
Tensile Stress
屈服
ISO527-2/1A/5
Mpa
2
Tensile Stress
--
ASTMD638
Mpa
2
Tensile Elongation
断裂4
ASTMD638
%
2
Tensile Elongation
断裂
ISO527-2/1A/5
%
2
Flexural Modulus
--
ASTMD790
Mpa
1
Flexural Modulus
--
ISO178
Mpa
2
Flexural Strength
--
ASTMD790
Mpa
3
Flexural Strength
--
ISO178
Mpa
3
Compressive Strength
ASTMD695
Mpa
1
Thermal Properties
Test Condition
Test Method
Unit
PEEK/SOLVAY USA/KT-820CF30
Specific Heat
50°C
DSC
J/kg/°C
1
Specific Heat
200°C
DSC
J/kg/°C
1
Glass Transition Temperature
ASTMD3418
°C
1
Thermal Conductivity
ASTME1530
W/m/K
0
Deflection Temperature Under Load?
1.8MPa,退火
ASTMD648
°C
3
Peak Melting Temperature
ASTMD3418
°C
3
Linear thermal expansion coefficient
MD：-50到50°C
ASTME831
cm/cm/°C
5
Fill Analysis
Test Condition
Test Method
Unit
PEEK/SOLVAY USA/KT-820CF30
Melt Viscosity
400°C,1000sec^-1
ASTMD3835
Pa·s
9
Impact Properties
Test Condition
Test Method
Unit
PEEK/SOLVAY USA/KT-820CF30
Unnotched Izod Impact Strength
--
ASTMD4812
J/m
7
Unnotched Izod Impact Strength
--
ISO180
kJ/m²
4