PEEK KetaSpire® PEEK KT-820CF30 SOLVAY USA
83
- Unit Price:
- $87409 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 22MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Filler: Carbon fiber rein 30% filler by weight
- Application Areas:Solvay Solvie Belgium
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD:3.18mm | ASTMD955 | 0.0到0.20 | % |
| TD:3.18mm | ASTMD955 | 1.5到1.7 | % | |
| Moisture Absorption | 24hr | ASTMD570 | 0.10 | % |
| Melt Mass-Flow Rate | 400°C/2.16kg | ASTMD1238 | 1.1 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress | Yield | ISO527-2/1A/5 | 217 | Mpa |
| -- | ASTMD638 | 201 | Mpa | |
| Tensile Modulus | --4 | ASTMD638 | 19700 | Mpa |
| -- | ISO527-2/1A/1 | 22800 | Mpa | |
| Tensile Elongation | Break | ISO527-2/1A/5 | 2.0 | % |
| Break4 | ASTMD638 | 2.0 | % | |
| Flexural Modulus | -- | ASTMD790 | 17500 | Mpa |
| -- | ISO178 | 20500 | Mpa | |
| Flexural Strength | -- | ASTMD790 | 317 | Mpa |
| -- | ISO178 | 311 | Mpa | |
| Compressive Strength | ASTMD695 | 173 | Mpa | |
| Shearing Strength | ASTMD732 | 95.1 | Mpa | |
| Poisson Ratio | 7.58 | 0.42 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Specific Heat | 50°C | DSC | 1130 | J/kg/°C |
| 200°C | DSC | 1620 | J/kg/°C | |
| Thermal Conductivity | ASTME1530 | 0.37 | W/m/K | |
| Deflection Temperature Under Load? | 1.8MPa,Annealed | ASTMD648 | 315 | °C |
| Linear thermal expansion coefficient | MD：-50to50°C | ASTME831 | 5.2E-06 | cm/cm/°C |
| Peak Melting Temperature | ASTMD3418 | 340 | °C | |
| Glass Transition Temperature | ASTMD3418 | 150 | °C |
| Fill Analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Viscosity | 400°C,1000sec^-1 | ASTMD3835 | 920 | Pa·s |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Unnotched Izod Impact Strength | -- | ASTMD4812 | 750 | J/m |
| -- | ISO180 | 44 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | M-Scale | ASTMD785 | 105 | |
| Shore Hardness | Shore D,1sec | ASTMD2240 | 92 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL94 | V-0 | |
| 1.6mm | UL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.