Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate (220°C 10kg) | / | ASTM D 1238 | 20.621 | g/10 min |
| Melt Mass-Flow Rate | 220°C/10.0 kg | ASTM D1238 | 21 | g/10 min |
| Modeling Shrinkage - Flow | 23°C, 3.20 mm, 注塑 | ASTM D955 | 0.40 到 0.70 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Elongation | 屈服, 23°C, 3.20 mm, 注塑 | ASTM D638 | > 5.0 | % |
| Tensile Elongation | 断裂, 23°C, 3.20 mm, 注塑 | ASTM D638 | 15 | % |
| Tensile Strength(Yield) | 3.2mm, 5 | ASTM D638 | 470 | kg/cm2 |
| Tensile Elongation (Break) | 3.2mm, 5 | ASTM D638 | 30 | % |
| Tensile Modulus | 23°C, 3.20 mm, 注塑 | ASTM D638 | 2050 | Mpa |
| Flexural Modulus | 3.2mm, 1 | ASTM D790 | 22000 | kg/cm2 |
| Flexural Modulus | 23°C, 3.20 mm, 注塑 | ASTM D790 | 2250 | Mpa |
| Flexural Strength | 23°C, 3.20 mm, 注塑 | ASTM D790 | 71.0 | Mpa |
| Flexural Strength | 3.2mm, 1 | ASTM D790 | 700 | kg/cm2 |
| Tensile Strength | 屈服, 23°C, 3.20 mm, 注塑 | ASTM D638 | 48.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ASTM D15257 | 89.0 | °C |
| RTI | | UL 746 | 50.0 | °C |
| RTI Imp | | UL 746 | 50.0 | °C |
| RTI Elec | | UL 746 | 50.0 | °C |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 6.40 mm, 注塑 | ASTM D648 | 81.0 | °C |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|
| Drying Time | | | 2.0 到 4.0 | hr |
| Rear Temperature | | | 180 到 200 | °C |
| Middle Temperature | | | 190 到 210 | °C |
| Front Temperature | | | 200 到 220 | °C |
| Nozzle Temperature | | | 190 到 220 | °C |
| Back Pressure | | | 29.4 到 58.8 | Mpa |
| Screw Speed | | | 30 到 60 | rpm |
| Drying Temperature | | | 80 到 90 | °C |
| Processing (Melt) Temp | | | 190 到 220 | °C |
| Mold Temperature | | | 40 到 60 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod Impact Strength 23℃ | 3.2mm | ASTM D256 | 17 | kg·cm/cm |
| Notched Izod Impact Strength 23℃ | 6.4mm | ASTM D256 | 17 | kg·cm/cm |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness R | | | 107 | |
| Rockwell Hardness | R 级, 23°C, 注塑 | ASTM D785 | 107 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Transmittance | 3200 µm, 注塑 | ASTM D1003 | 90.0 | % |
| Transmittance |
Rate B/50 | ASTM D1003 | 90 | % |
| Haze | -40°C to | ASTM D1003 | 2 | % |
| Haze | 注塑 | ASTM D1003 | 2.0 | % |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | 1.5 mm | UL 94 | HB | |
| Flame Rating | 3.0 mm | UL 94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.