Physical Properties
Test Condition
Test Method
Unit
MABS/LG CHEM KOREA/TR557
Melt Mass-Flow Rate
220°C/10.0 kg
ASTM D1238
g/10 min
2
Melt Mass-Flow Rate (220°C 10kg)
/
ASTM D 1238
g/10 min
2
Modeling Shrinkage - Flow
23°C, 3.20 mm, 注塑
ASTM D955
%
0
Mechanical Properties
Test Condition
Test Method
Unit
MABS/LG CHEM KOREA/TR557
Tensile Strength
屈服, 23°C, 3.20 mm, 注塑
ASTM D638
Mpa
4
Tensile Modulus
23°C, 3.20 mm, 注塑
ASTM D638
Mpa
2
Tensile Strength(Yield)
3.2mm, 5
ASTM D638
kg/cm2
4
Tensile Elongation (Break)
3.2mm, 5
ASTM D638
%
3
Tensile Elongation
屈服, 23°C, 3.20 mm, 注塑
ASTM D638
%
>
Tensile Elongation
断裂, 23°C, 3.20 mm, 注塑
ASTM D638
%
1
Flexural Modulus
23°C, 3.20 mm, 注塑
ASTM D790
Mpa
2
Flexural Modulus
3.2mm, 1
ASTM D790
kg/cm2
2
Flexural Strength
3.2mm, 1
ASTM D790
kg/cm2
7
Flexural Strength
23°C, 3.20 mm, 注塑
ASTM D790
Mpa
7
Thermal Properties
Test Condition
Test Method
Unit
MABS/LG CHEM KOREA/TR557
RTI
UL 746
°C
5
RTI Elec
UL 746
°C
5
RTI Imp
UL 746
°C
5
Vicat Softening Temperature
ASTM D15257
°C
8
Deflection Temperature Under Load?
1.8 MPa, 未退火, 6.40 mm, 注塑
ASTM D648
°C
8
Impact Properties
Test Condition
Test Method
Unit
MABS/LG CHEM KOREA/TR557
Notched Izod Impact Strength 23℃
3.2mm
ASTM D256
kg·cm/cm
1
Notched Izod Impact Strength 23℃
6.4mm
ASTM D256
kg·cm/cm
1
Injection
Test Condition
Test Method
Unit
MABS/LG CHEM KOREA/TR557
Back Pressure
Mpa
2
Drying Time
hr
2
Drying Temperature
°C
8
Processing (Melt) Temp
°C
1
Rear Temperature
°C
1
Front Temperature
°C
2
Middle Temperature
°C
1
Screw Speed
rpm
3
Mold Temperature
°C
4
Nozzle Temperature
°C
1
optical performance
Test Condition
Test Method
Unit
MABS/LG CHEM KOREA/TR557
Transmittance
Rate B/50
ASTM D1003
%
9
Transmittance
3200 µm, 注塑
ASTM D1003
%
9
Haze
注塑
ASTM D1003
%
2
Haze
-40°C to
ASTM D1003
%
2