Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:--

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt Mass-Flow Rate (220°C 10kg)	/	ASTM D 1238	20.621	g/10 min
Melt Mass-Flow Rate	220°C/10.0 kg	ASTM D1238	21	g/10 min
Modeling Shrinkage - Flow	23°C, 3.20 mm, Injection	ASTM D955	0.40 到 0.70	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Elongation	Yield, 23°C, 3.20 mm, Injection	ASTM D638	> 5.0	%
Tensile Elongation	Tensile Elongation	Break, 23°C, 3.20 mm, Injection	ASTM D638	15	%
Tensile Strength(Yield)	3.2mm, 5	ASTM D638	470	kg/cm2
Tensile Elongation (Break)	3.2mm, 5	ASTM D638	30	%
Tensile Modulus	23°C, 3.20 mm, Injection	ASTM D638	2050	Mpa
Flexural Modulus	3.2mm, 1	ASTM D790	22000	kg/cm2
Flexural Modulus	Flexural Modulus	23°C, 3.20 mm, Injection	ASTM D790	2250	Mpa
Flexural Strength	23°C, 3.20 mm, Injection	ASTM D790	71.0	Mpa
Flexural Strength	Flexural Strength	3.2mm, 1	ASTM D790	700	kg/cm2
Tensile Strength	Yield, 23°C, 3.20 mm, Injection	ASTM D638	48.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature		ASTM D15257	89.0	°C
RTI		UL 746	50.0	°C
RTI Imp		UL 746	50.0	°C
RTI Elec		UL 746	50.0	°C
Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm, Injection	ASTM D648	81.0	°C

Injection	Test Result	Unit
Drying Time	2.0 到 4.0	hr
Rear Temperature	180 到 200	°C
Middle Temperature	190 到 210	°C
Front Temperature	200 到 220	°C
Nozzle Temperature	190 到 220	°C
Back Pressure	29.4 到 58.8	Mpa
Screw Speed	30 到 60	rpm
Drying Temperature	80 到 90	°C
Processing (Melt) Temp	190 到 220	°C
Mold Temperature	40 到 60	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Notched Izod Impact Strength 23℃	3.2mm	ASTM D256	17	kg·cm/cm
Notched Izod Impact Strength 23℃	Notched Izod Impact Strength 23℃	6.4mm	ASTM D256	17	kg·cm/cm

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness R			107
Rockwell Hardness	R-Scale, 23°C, Injection	ASTM D785	107

optical performance	Test Condition	Test Method	Test Result	Unit
Transmittance	3200 μm, Injection	ASTM D1003	90.0	%
Transmittance	Rate B/50	ASTM D1003	90	%
Haze	-40°C to	ASTM D1003	2	%
Haze	Haze	Injection	ASTM D1003	2.0	%

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	1.5 mm	UL 94	HB
Flame Rating	Flame Rating	3.0 mm	UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.