Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Apparent density | | ISO60 | 0.80 | g/cm³ |
| Melt volume flow rate | 260°C/5.0kg | ISO1133 | 20.0 | cm3/10min |
| Shrinkage rate | TD:250°C,2.00mm2 | ISO2577 | 0.80 | % |
| Shrinkage rate | TD:120°C,4小时,2.00mm3 | ISO2577 | 0.80 | % |
| Shrinkage rate | MD:250°C,2.00mm2 | ISO2577 | 0.80 | % |
| Shrinkage rate | MD:120°C,4小时,2.00mm3 | ISO2577 | 0.80 | % |
| Water absorption rate | 饱和,23°C | ISO62 | 0.30 | % |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.10 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | 23°C | ISO527-2/1 | 2000 | Mpa |
| Tensile stress | 屈服,23°C | ISO527-2/50 | 45.0 | Mpa |
| Tensile strain | 屈服,23°C | ISO527-2/50 | 3.5 | % |
| Nominal tensile fracture strain | 23°C | ISO527-2/50 | >20 | % |
| Bending modulus 4 | 23°C | ISO178/A | 2000 | Mpa |
| Bending stress | 3.5%Strain,23°C | ISO178/A | 65.0 | Mpa |
| Bending stress | 23°C4 | ISO178/A | 70.0 | Mpa |
| Bending strain 5 | 23°C | ISO178/A | 5.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear coefficient of thermal expansion | MD：23到55°C | ISO11359-2 | 1E-04 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO11359-2 | 1.1E-04 | cm/cm/°C |
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 100 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 75.0 | °C |
| Vicat softening temperature | | ISO306/B120 | 115 | °C |
| Melting temperature 5 | | ISO11357-3 | 225 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Leakage Trace Index | 解决方案A | IEC60112 | 600 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | NoBreak | |
| Unscented Izod impact strength | -30°C | ISO180/1U | NoBreak | |
| Unscented Izod impact strength | 23°C | ISO180/1U | NoBreak | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | NoBreak | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball pressure hardness | | ISO2039-1 | 93.0 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.8mm | UL94 | V-0 | |
| Burning wire flammability index | 0.8mm | IEC60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 0.8mm | IEC60695-2-13 | 775 | °C |
| Hot filament ignition temperature | 1.6mm | IEC60695-2-13 | 775 | °C |
| Hot filament ignition temperature | 3.0mm | IEC60695-2-13 | 775 | °C |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| ISO Shortcut | | ISO7792 | PBT+PC,GFHLMPR,11-020 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.