Apparent density

ISO60

g/cm³

0

Melt volume flow rate

260°C/5.0kg

ISO1133

cm3/10min

2

Shrinkage rate

TD:250°C,2.00mm2

ISO2577

%

0

Shrinkage rate

TD:120°C,4小时,2.00mm3

ISO2577

%

0

Shrinkage rate

MD:250°C,2.00mm2

ISO2577

%

0

Shrinkage rate

MD:120°C,4小时,2.00mm3

ISO2577

%

0

Water absorption rate

饱和,23°C

ISO62

%

0

Water absorption rate

平衡,23°C,50%RH

ISO62

%

0

Nominal tensile fracture strain

23°C

ISO527-2/50

%

>

Tensile modulus

23°C

ISO527-2/1

Mpa

2

Tensile strain

屈服,23°C

ISO527-2/50

%

3

Tensile stress

屈服,23°C

ISO527-2/50

Mpa

4

Bending modulus 4

23°C

ISO178/A

Mpa

2

Bending strain 5

23°C

ISO178/A

%

5

Bending stress

3.5%Strain,23°C

ISO178/A

Mpa

6

Bending stress

23°C4

ISO178/A

Mpa

7

Hot deformation temperature

0.45MPa,未退火

ISO75-2/B

°C

1

Hot deformation temperature

1.8MPa,未退火

ISO75-2/A

°C

7

Melting temperature 5

ISO11357-3

°C

2

Vicat softening temperature

ISO306/B120

°C

1

Linear coefficient of thermal expansion

MD：23到55°C

ISO11359-2

cm/cm/°C

1

Linear coefficient of thermal expansion

TD：23to55°C

ISO11359-2

cm/cm/°C

1

Leakage Trace Index

解决方案A

IEC60112

V

6

Ball pressure hardness

ISO2039-1

Mpa

9

Hot filament ignition temperature

0.8mm

IEC60695-2-13

°C

7

Hot filament ignition temperature

1.6mm

IEC60695-2-13

°C

7

Hot filament ignition temperature

3.0mm

IEC60695-2-13

°C

7

Burning wire flammability index

0.8mm

IEC60695-2-12

°C

9