ABS/PBT Pocan® KU2-7604 LANXESS GERMANY

172

Unit Price:
$2263 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
33MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Low warpage Flame retardant
Application Areas:Electrical and electronic
Color:--
Grade:Flame retardant

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Apparent density		ISO60	0.80	g/cm³
Melt volume flow rate	260°C/5.0kg	ISO1133	20.0	cm3/10min
Shrinkage rate	TD:250°C,2.00mm2	ISO2577	0.80	%
	Shrinkage rate	TD:120°C,4hr,2.00mm3	ISO2577	0.80	%
		Shrinkage rate	MD:250°C,2.00mm2	ISO2577	0.80	%
		Shrinkage rate	Shrinkage rate	MD:120°C,4hr,2.00mm3	ISO2577	0.80	%
Water absorption rate	Saturation,23°C	ISO62	0.30	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO62	0.10	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	23°C	ISO527-2/1	2000	Mpa
Tensile stress	Yield,23°C	ISO527-2/50	45.0	Mpa
Tensile strain	Yield,23°C	ISO527-2/50	3.5	%
Nominal tensile fracture strain	23°C	ISO527-2/50	>20	%
Bending modulus 4	23°C	ISO178/A	2000	Mpa
Bending stress	3.5%Strain,23°C	ISO178/A	65.0	Mpa
Bending stress	Bending stress	23°C4	ISO178/A	70.0	Mpa
Bending strain 5	23°C	ISO178/A	5.0	%

Thermal performance	Test Condition	Test Method	Test Result	Unit
Linear coefficient of thermal expansion	MD：23to55°C	ISO11359-2	1E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO11359-2	1.1E-04	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	100	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	75.0	°C
Vicat softening temperature		ISO306/B120	115	°C
Melting temperature 5		ISO11357-3	225	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Leakage Trace Index	SolutionA	IEC60112	600	V

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	23°C	ISO179/1eU	NoBreak
Unscented Izod impact strength	-30°C	ISO180/1U	NoBreak
Unscented Izod impact strength	Unscented Izod impact strength	23°C	ISO180/1U	NoBreak
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	NoBreak

hardness	Test Condition	Test Method	Test Result	Unit
Ball pressure hardness		ISO2039-1	93.0	Mpa

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.8mm	UL94	V-0
Burning wire flammability index	0.8mm	IEC60695-2-12	960	°C
Hot filament ignition temperature	0.8mm	IEC60695-2-13	775	°C
	Hot filament ignition temperature	1.6mm	IEC60695-2-13	775	°C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC60695-2-13	775	°C

Supplementary Information	Test Condition	Test Method	Test Result	Unit
ISO Shortcut		ISO7792	PBT+PC,GFHLMPR,11-020

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.