Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt volume flow rate | 250°C/5.0kg | ISO1133 | 2.00 | cm3/10min |
| Melt volume flow rate | 250°C/5.0kg | ISO1133 | 4.00 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | | ISO527-2/1A/1 | 3300 | Mpa |
| Tensile modulus | | ISO527-2/1A/1 | 4900 | Mpa |
| Tensile stress | 屈服 | ISO527-2/1A/50 | 43.0 | Mpa |
| Tensile stress | 断裂 | ISO527-2/1A/5 | 77.0 | Mpa |
| Tensile strain | 断裂 | ISO527-2/1A/5 | 4.5 | % |
| Tensile strain | 屈服 | ISO527-2/1A/50 | 3.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | -- | ISO306/A50 | 190 | °C |
| Vicat softening temperature | -- | ISO306/B50 | 115 | °C |
| Vicat softening temperature | -- | ISO306/A50 | 213 | °C |
| Vicat softening temperature | -- | ISO306/B50 | 128 | °C |
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/Bf | 152 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/Af | 76.0 | °C |
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/Bf | 179 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/Af | 101 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | IEC60093 | >1.0E+15 | ohms |
| Volume resistivity | | IEC60093 | >1.0E+13 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 36 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 70 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball pressure hardness | H358/30 | ISO2039-1 | 97.0 | Mpa |
| Ball pressure hardness | H358/30 | ISO2039-1 | 93.0 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.6mm | IEC60695-11-10,-20 | HB | |
| Burning rate | | ISO3795 | <100 | mm/min |
| Flammability level | 1.5mm | IEC60695-11-10,-20 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.