Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS/PA M/MK 8 A SCHULMAN USA
SCHULABLEND®
--
Filler: Glass fiber reinf、8.0% filler by weight、20% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ABS/PA/A SCHULMAN USA/M/MK 8
Melt volume flow rate
250°C/5.0kg
ISO1133
cm3/10min
4
Melt volume flow rate
250°C/5.0kg
ISO1133
cm3/10min
2
Mechanical performance
Test Condition
Test Method
Unit
ABS/PA/A SCHULMAN USA/M/MK 8
Tensile modulus
ISO527-2/1A/1
Mpa
4
Tensile modulus
ISO527-2/1A/1
Mpa
3
Tensile strain
屈服
ISO527-2/1A/50
%
3
Tensile strain
断裂
ISO527-2/1A/5
%
4
Tensile stress
屈服
ISO527-2/1A/50
Mpa
4
Tensile stress
断裂
ISO527-2/1A/5
Mpa
7
Thermal performance
Test Condition
Test Method
Unit
ABS/PA/A SCHULMAN USA/M/MK 8
Hot deformation temperature
0.45MPa,未退火
ISO75-2/Bf
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/Af
°C
1
Hot deformation temperature
0.45MPa,未退火
ISO75-2/Bf
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/Af
°C
7
Vicat softening temperature
--
ISO306/A50
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Vicat softening temperature
--
ISO306/A50
°C
2
Vicat softening temperature
--
ISO306/B50
°C
1
Electrical performance
Test Condition
Test Method
Unit
ABS/PA/A SCHULMAN USA/M/MK 8
Surface resistivity
IEC60093
ohms
>
Volume resistivity
IEC60093
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
ABS/PA/A SCHULMAN USA/M/MK 8
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
7
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
3
hardness
Test Condition
Test Method
Unit
ABS/PA/A SCHULMAN USA/M/MK 8
Ball pressure hardness
H358/30
ISO2039-1
Mpa
9
Ball pressure hardness
H358/30
ISO2039-1
Mpa
9
flammability
Test Condition
Test Method
Unit
ABS/PA/A SCHULMAN USA/M/MK 8
Burning rate
ISO3795
mm/min
<