ABS/PA SCHULABLEND® M/MK 8 A SCHULMAN USA
179
- Unit Price:
- $2506 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Filler: Glass fiber reinf 8.0% filler by weight 20% filler by weight
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt volume flow rate | 250°C/5.0kg | ISO1133 | 4.00 | cm3/10min |
| 250°C/5.0kg | ISO1133 | 2.00 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2/1A/1 | 3300 | Mpa | |
| Tensile stress | Yield | ISO527-2/1A/50 | 43.0 | Mpa |
| Tensile strain | Yield | ISO527-2/1A/50 | 3.0 | % |
| Tensile modulus | ISO527-2/1A/1 | 4900 | Mpa | |
| Tensile stress | Break | ISO527-2/1A/5 | 77.0 | Mpa |
| Tensile strain | Break | ISO527-2/1A/5 | 4.5 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/Bf | 179 | °C |
| 1.8MPa,Unannealed | ISO75-2/Af | 101 | °C | |
| Vicat softening temperature | -- | ISO306/A50 | 213 | °C |
| -- | ISO306/B50 | 128 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/Bf | 152 | °C |
| 1.8MPa,Unannealed | ISO75-2/Af | 76.0 | °C | |
| Vicat softening temperature | -- | ISO306/A50 | 190 | °C |
| -- | ISO306/B50 | 115 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+13 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 70 | kJ/m² |
| 23°C | ISO179/1eU | 36 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | H358/30 | ISO2039-1 | 93.0 | Mpa |
| H358/30 | ISO2039-1 | 97.0 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.6mm | IEC60695-11-10,-20 | HB | |
| Burning rate | ISO3795 | <100 | mm/min | |
| Flammability level | 1.5mm | IEC60695-11-10,-20 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.