Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate | 饱和,23°C,2.00mm | ISO62 | 4.9 | % |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO62 | 1.5 | % |
| Shrinkage rate | TD | ISO294-4 | 0.90 | % |
| Shrinkage rate | MD | ISO294-4 | 0.10 | % |
| Density/specific gravity | | ISO1183 | 1.51 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile creep modulus | 1000hr | ISO899-1 | -- | Mpa |
| TensileCreepModule | 1hr | ISO899-1 | -- | Mpa |
| Tensile stress | 断裂 | ISO527-2 | 230 | Mpa |
| Tensile strain | 断裂 | ISO527-2 | 3.0 | % |
| Tensile modulus | | ISO527-2 | 14500 | Mpa |
| Bending modulus | | ISO178 | 13000 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 221 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 213 | °C |
| Vicat softening temperature | | ISO306/B50 | 215 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.6E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD | ISO11359-2 | 1E-04 | cm/cm/°C |
| Melting temperature 2 | | ISO11357-3 | 221 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 120 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 120 | kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 19 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 20 | kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 15 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 18 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| FMVSS flammability | | FMVSS302 | B | |
| Burning rate 3 | 1.00mm | ISO3795 | 44 | mm/min |
| Flammability level | 1.5mm | IEC60695-11-10,-20 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.