Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 73G45L DUPONT USA
Zytel®
Electronic and electrical、Automotive Applications
Thermal stability、Filler: Glass fiber reinf、45% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA6/DUPONT USA/73G45L
Density/specific gravity
ISO1183
g/cm³
1
Shrinkage rate
TD
ISO294-4
%
0
Shrinkage rate
MD
ISO294-4
%
0
Water absorption rate
饱和,23°C,2.00mm
ISO62
%
4
Water absorption rate
平衡,23°C,2.00mm,50%RH
ISO62
%
1
Mechanical performance
Test Condition
Test Method
Unit
PA6/DUPONT USA/73G45L
TensileCreepModule
1hr
ISO899-1
Mpa
-
Tensile modulus
ISO527-2
Mpa
1
Tensile creep modulus
1000hr
ISO899-1
Mpa
-
Tensile strain
断裂
ISO527-2
%
3
Tensile stress
断裂
ISO527-2
Mpa
2
Bending modulus
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PA6/DUPONT USA/73G45L
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Melting temperature 2
ISO11357-3
°C
2
Vicat softening temperature
ISO306/B50
°C
2
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
TD
ISO11359-2
cm/cm/°C
1
Impact performance
Test Condition
Test Method
Unit
PA6/DUPONT USA/73G45L
Charpy Notched Impact Strength
-30°C
ISO179/1eA
kJ/m²
1
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
2
Impact strength of simply supported beam without notch
-30°C
ISO179/1eU
kJ/m²
1
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
1
Impact strength of cantilever beam gap
-30°C
ISO180/1A
kJ/m²
1
Impact strength of cantilever beam gap
23°C
ISO180/1A
kJ/m²
1
flammability
Test Condition
Test Method
Unit
PA6/DUPONT USA/73G45L
Burning rate 3
1.00mm
ISO3795
mm/min
4