Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | | ASTM D-955 | 0.4 | % |
| Modeling Shrinkage | MD | ASTMD955 | <0.40 | % |
| Moisture Absorption | 24hr | ASTMD570 | <0.30 | % |
| Melt Mass-Flow Rate | 200°C/5.0kg | ASTMD1238 | 0.80 | g/10min |
| Melt Mass-Flow Rate | 220°C/10.0kg | ASTMD1238 | 8.0 | g/10min |
| Density / Specific Gravity | | ASTMD792 | 1.03 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Strength | 屈服,23°C | ASTMD790 | 58.6 | Mpa |
| Tensile Strength(Yield) | 23℃ | ASTM D-638 | 350 | kg/cm |
| Tensile Strength(Yield) | 23℃ | ASTM D-638 | 5000 | psi |
| Flexural Modulus | 23°C | ASTMD790 | 2000 | Mpa |
| Tensile Strength (Break) | 1/8" | ASTM D-638 | 4300 | kg/cm |
| Tensile Strength (Break) | 1/8" | ASTM D-638 | 300 | psi |
| Tensile Strength | 屈服,23°C,3.18mm | ASTMD638 | 32.4 | Mpa |
| Tensile Elongation | 断裂,23°C,3.18mm | ASTMD638 | 90 | % |
| Tensile Strength | Break,23°C,3.18mm | ASTMD638 | 27.6 | Mpa |
| Tensile Strength | 23℃ 2.8mm/min | ASTM D-790 | 20000 | kg/cm |
| Tensile Strength | 23℃ 2.8mm/min | ASTM D-790 | 290000 | psi |
| IZOD Notch Impact Strength | 23℃1/2" | ASTM D-256 | 38 (7.0) | kg.cm/cm(ft.1b/in) |
| IZOD Notch Impact Strength | 23℃1/8" | ASTM D-256 | 53 (9.8) | kg.cm/cm(ft.1b/in) |
| Tensile Strength | 23℃ 2.8mm/min | ASTM D-790 | 600 | kg/cm |
| Tensile Strength | 23℃ 2.8mm/min | ASTM D-790 | 8500 | psi |
| Tensile Elongation?(Break) | 1/8" | ASTM D-638 | 50 | % |
| Rockwell Hardness | | | 100 | |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8MPa,未退火,12.7mm | ASTMD648 | 85.0 | °C |
| Deflection Temperature Under Load? | 未退火 | ASTM D-1525 | 85(185) | ℃(F) |
| Vicat Softening Temperature | | ASTM D-1525 | 100 | °C |
| Vicat Softening Temperature | | ASTMD15254 | 102 | °C |
| Flame Rating | | UL94 | HB | |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod Impact Strength | 23°C,6.35mm | ASTMD256 | 450 | J/m |
| Notched Izod Impact Strength | 23°C,3.18mm | ASTMD256 | 490 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R计秤,23°C | ASTMD785 | 100 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | 1.6mm | UL94 | HB | |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Density / Specific Gravity | | ASTM D-792 | 1.03 | |
| Moisture Absorption | | ASTM D-570 | 0.3 | wt% |
| Melt index | 200℃/5kg | ASTM D-1238 | 0.8 | g/10min |
| Melt index | 200℃/5kg | ASTM D-1238 | 8.0 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.