ABS TAITALAC® 3100 TAIDA TAIWAN
96
- Unit Price:
- $2502 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Excellent hot forming Ultra high impact resista Widely used for extrusion Ultra high impact strengt Good processability
- Application Areas:Helmet Low temperature products Toolbox Bus box Locomotive parts Application in the automo heel Footwear Controlled pipe fittings Used for luggage
- Color:--
- Grade:Heat resistant grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | ASTM D-955 | 0.4 | % | |
| MD | ASTMD955 | <0.40 | % | |
| Water absorption rate | 24hr | ASTMD570 | <0.30 | % |
| Melt mass flow rate | 200°C/5.0kg | ASTMD1238 | 0.80 | g/10min |
| 220°C/10.0kg | ASTMD1238 | 8.0 | g/10min | |
| Density/specific gravity | ASTMD792 | 1.03 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending strength 4 | Yield,23°C | ASTMD790 | 58.6 | Mpa |
| Tensile strength at the point of surrender | 23℃ | ASTM D-638 | 350 | kg/cm |
| 23℃ | ASTM D-638 | 5000 | psi | |
| Bending modulus 3 | 23°C | ASTMD790 | 2000 | Mpa |
| Tensile strength at fracture point | 1/8" | ASTM D-638 | 4300 | kg/cm |
| 1/8" | ASTM D-638 | 300 | psi | |
| Tensile strength 2 | Yield,23°C,3.18mm | ASTMD638 | 32.4 | Mpa |
| Elongation rate 2 | Break,23°C,3.18mm | ASTMD638 | 90 | % |
| Tensile strength 2 | Break,23°C,3.18mm | ASTMD638 | 27.6 | Mpa |
| Flexural coefficient | 23℃ 2.8mm/min | ASTM D-790 | 20000 | kg/cm |
| 23℃ 2.8mm/min | ASTM D-790 | 290000 | psi | |
| IZOD notch impact strength | 23℃1/2" | ASTM D-256 | 38 (7.0) | kg.cm/cm(ft.1b/in) |
| 23℃1/8" | ASTM D-256 | 53 (9.8) | kg.cm/cm(ft.1b/in) | |
| Flexural strength | 23℃ 2.8mm/min | ASTM D-790 | 600 | kg/cm |
| 23℃ 2.8mm/min | ASTM D-790 | 8500 | psi | |
| elongation at break | 1/8" | ASTM D-638 | 50 | % |
| Rockwell hardness | 100 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed,12.7mm | ASTMD648 | 85.0 | °C |
| Unannealed | ASTM D-1525 | 85(185) | ℃(F) | |
| vicat softening point | ASTM D-1525 | 100 | °C | |
| Vicat softening temperature | ASTMD15254 | 102 | °C | |
| Flame retardant grade | UL94 | HB |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTMD256 | 450 | J/m |
| 23°C,3.18mm | ASTMD256 | 490 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Sale,23°C | ASTMD785 | 100 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 1.6mm | UL94 | HB |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | ASTM D-792 | 1.03 | ||
| Water absorption rate | ASTM D-570 | 0.3 | wt% | |
| Melt index | 200℃/5kg | ASTM D-1238 | 0.8 | g/10min |
| 200℃/5kg | ASTM D-1238 | 8.0 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.