Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 饱和,23°C | ISO62 | 0.40 | % |
| | 内部方法 | 10.0 | CM |
| Modeling Shrinkage | TD | ISO294-4 | 0.90 | % |
| Modeling Shrinkage | MD | ISO294-4 | 0.30 | % |
| Moisture Absorption | 100°C | ISO62 | 0.45 | % |
| Density / Specific Gravity | | ISO1183 | 1.43 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | 断裂,23°C | ISO527-2 | 160 | Mpa |
| Tensile Strain | 断裂,23°C | ISO527-2 | 3.4 | % |
| Tensile Modulus | 23°C | ISO527-2 | 8800 | Mpa |
| Flexural Modulus | 23°C | ISO178 | 8300 | Mpa |
| Flexural Stress | 23°C | ISO178 | 250 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Glass Transition Temperature | --7 | ISO11357-2 | 143 | °C |
| Glass Transition Temperature | --8 | ISO11357-2 | 150 | °C |
| Linear thermal expansion coefficient | MD:<143°C | ISO11359-2 | 2E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | MD:>143°C | ISO11359-2 | 2.2E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | TD:<143°C | ISO11359-2 | 4.5E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | TD:>143°C | ISO11359-2 | 1.2E-04 | cm/cm/°C |
| Melting temperature | | ISO11357-3 | 343 | °C |
| Deflection Temperature Under Load? | 1.8MPa,未退火 | ISO75-2/Af | 315 | °C |
| Thermal Conductivity | 23°C9 | ISO22007-4 | 0.30 | W/m/K |
| Thermal Conductivity | 23°C10 | ISO22007-4 | 0.35 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Comparative Tracking Index | | IEC60112 | 150 | V |
| Dielectric Constant | 23°C,1kHz | IEC60250 | 3.10 | |
| Volume Resistivity | | IEC60093 | 1E+16 | ohms·cm |
| Dissipation Factor? | 23°C,1MHz | IEC60250 | 5E-03 | |
| Dielectric Strength | 2.00mm | IEC60243-1 | 24 | KV/mm |
| Fill Analysis | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Viscosity | 400°C | ISO11443 | 475 | Pa·s |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod impact strength | 23°C | ISO180 | 65 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/A | 10 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | 邵氏D,23°C | ISO868 | 86 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.