Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | 横向流量 | 内部方法 | 0.30 到 0.70 | % |
| Modeling Shrinkage | 流量 | 内部方法 | 0.10 到 0.40 | % |
| Moisture Absorption | 平衡, 23°C, 50% RH | ISO 62 | 0.020 | % |
| Density | | ISO 1183 | 1.45 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Stress | | ISO 178 | 170 | Mpa |
| Tensile Stress | 断裂 | ISO 527-2 | 110 | Mpa |
| Tensile Strain | 断裂 | ISO 527-2 | 1.5 | % |
| Tensile Modulus | | ISO 527-2 | 10500 | Mpa |
| Flexural Modulus | | ISO 178 | 10300 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45 MPa, 未退火 | ISO 75-2/B | 265 | °C |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火 | ISO 75-2/A | 230 | °C |
| RTI | | UL 746 | 130 | °C |
| RTI Imp | | UL 746 | 120 | °C |
| RTI Elec | | UL 746 | 130 | °C |
| Linear thermal expansion coefficient | 流动 : -30 到 30°C | TMA | 1.9E-5 | cm/cm/°C |
| Linear thermal expansion coefficient | 横向 : -30 到 30°C | TMA | 4.2E-5 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Strength | | ASTM D149 | 35 | KV/mm |
| Hot-wire Ignition | 0.75 mm | UL 746 | PLC 3 | |
| Hot-wire Ignition | 1.5 mm | UL 746 | PLC 2 | |
| High Voltage Arc Tracking Rate | | UL 746 | PLC 3 | |
| Comparative Tracking Index | | IEC 60112 | PLC 1 | |
| Dissipation Factor? | 1 MHz | IEC 60250 | 2.0E-3 | |
| High Amp Arc Ignition | 0.75 mm | UL 746 | PLC 0 | |
| High Amp Arc Ignition | 1.5 mm | UL 746 | PLC 0 | |
| Dielectric Constant | 1 MHz | IEC 60250 | 3.00 | |
| Arc Resistance | | ASTM D495 | PLC 6 | |
| Volume Resistivity | | IEC 60093 | > 1.0E+16 | ohms·cm |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|
| Drying Temperature | | | 120 | °C |
| Processing (Melt) Temp | | | 280 到 310 | °C |
| Mold Temperature | | | 130 到 155 | °C |
| Drying Time | | | 3.0 到 5.0 | hr |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | 23°C | ISO 179 | 28 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179 | 9.0 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO 180 | 8.0 | kJ/m² |
| Notched Izod impact strength | 23°C | ISO 180 | 26 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | > 0.75 mm | UL 94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.