SPS XAREC™ S931 IDEMITSU JAPAN

Unit Price:
$3417 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
33MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Across Flow	内部方法	0.30 到 0.70	%
Modeling Shrinkage	Modeling Shrinkage	流量	内部方法	0.10 到 0.40	%
Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.020	%
Density		ISO 1183	1.45	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress		ISO 178	170	Mpa
Tensile Stress	Break	ISO 527-2	110	Mpa
Tensile Strain	Break	ISO 527-2	1.5	%
Tensile Modulus		ISO 527-2	10500	Mpa
Flexural Modulus		ISO 178	10300	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45 MPa, Unannealed	ISO 75-2/B	265	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed	ISO 75-2/A	230	°C
RTI		UL 746	130	°C
RTI Imp		UL 746	120	°C
RTI Elec		UL 746	130	°C
Linear thermal expansion coefficient	Flow : -30 to 30°C	TMA	1.9E-5	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : -30 to 30°C	TMA	4.2E-5	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength		ASTM D149	35	KV/mm
Hot-wire Ignition	0.75 mm	UL 746	PLC 3
Hot-wire Ignition	Hot-wire Ignition	1.5 mm	UL 746	PLC 2
High Voltage Arc Tracking Rate		UL 746	PLC 3
Comparative Tracking Index		IEC 60112	PLC 1
Dissipation Factor?	1 MHz	IEC 60250	2.0E-3
High Amp Arc Ignition	0.75 mm	UL 746	PLC 0
High Amp Arc Ignition	High Amp Arc Ignition	1.5 mm	UL 746	PLC 0
Dielectric Constant	1 MHz	IEC 60250	3.00
Arc Resistance		ASTM D495	PLC 6
Volume Resistivity		IEC 60093	> 1.0E+16	ohms·cm

Injection	Test Result	Unit
Drying Temperature	120	°C
Processing (Melt) Temp	280 到 310	°C
Mold Temperature	130 到 155	°C
Drying Time	3.0 到 5.0	hr

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	23°C	ISO 179	28	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179	9.0	kJ/m²
Notched Izod Impact Strength	23°C	ISO 180	8.0	kJ/m²
Notched Izod impact strength	23°C	ISO 180	26	kJ/m²

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	> 0.75 mm	UL 94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.