PA66 Zytel® ST801AHS BK010 DUPONT USA
223
- Properties:High impact resistance
- Usages:Home appliance componentsAutomotive Applications
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | 横向流量 | ISO 294-4 | 1.4 | % |
| 流量 | ISO 294-4 | 1.8 | % | |
| Moisture Absorption | 24 hr, 23°C | ISO 62 | 1.1 | % |
| 饱和, 23°C, 2.00 mm | ISO 62 | 6.5 | % | |
| 平衡, 23°C, 2.00 mm, 50% RH | ISO 62 | 2.0 | % | |
| Viscosity number | ISO 307 | 130 | cm³/g | |
| Density | ISO 1183 | 1.07 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress | 50% 应变 | ISO 527-2 | 49.0 | Mpa |
| Tensile Strain | 断裂 | ISO 527-2 | > 50 | % |
| Tensile Creep Modulus | 1 hr | ISO 899-1 | -- | Mpa |
| 1000 hr | ISO 899-1 | -- | Mpa | |
| Tensile Modulus | ISO 527-2 | 2000 | Mpa | |
| Flexural Modulus | ISO 178 | 1800 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, 未退火 | ISO 75-2/B | 157 | °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 63.0 | °C | |
| Linear thermal expansion coefficient | 流动 : 23 到 55°C | ASTM E831 | 1.4E-4 | cm/cm/°C |
| 流动 | ISO 11359-2 | 1.4E-4 | cm/cm/°C | |
| 流动 : -40 到 23°C | ISO 11359-2 | 1.1E-4 | cm/cm/°C | |
| 流动 : 55 到 160°C | ISO 11359-2 | 1.6E-4 | cm/cm/°C | |
| 横向 : 23 到 55°C | ASTM E831 | 1.3E-4 | cm/cm/°C | |
| 横向 | ISO 11359-2 | 1.3E-4 | cm/cm/°C | |
| 横向 : -40 到 23°C | ISO 11359-2 | 1.1E-4 | cm/cm/°C | |
| 横向 : 55 到 160°C | ISO 11359-2 | 1.3E-4 | cm/cm/°C | |
| Vicat Softening Temperature | ISO 306/B50 | 205 | °C | |
| Glass Transition Temperature | ISO 11357-2 | 75.0 | °C | |
| Melting Temperature | ISO 11357-3 | 262 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation Factor? | 100 Hz | IEC 62631-2-1 | 5.0E-3 | |
| 1 MHz | IEC 62631-2-1 | 0.010 | ||
| Dielectric Strength | IEC 60243-1 | 25 | KV/mm | |
| Relative Permittivity | 1 MHz | IEC 62631-2-1 | 3.30 | |
| 100 Hz | IEC 62631-2-1 | 3.50 | ||
| Comparative Tracking Index | IEC 60112 | 600 | V | |
| Surface Resistivity | IEC 62631-3-2 | -- | ohms | |
| Volume Resistivity | IEC 62631-3-1 | > 1.0E+13 | ohms·m |
| Fill Analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ejection Temperature | 190 | °C |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature | 80 | °C | ||
| Drying time - Hot air dryer | 2.0 到 4.0 | hr | ||
| Suggested Max Moisture | 0.20 | % | ||
| Processing (Melt) Temp | 280 到 300 | °C | ||
| 290 | °C | |||
| Mold Temperature | 50 到 100 | °C | ||
| 80 | °C | |||
| Holding Pressure | 50.0 到 100 | Mpa | ||
| Drying Recommended | yes | |||
| 4.00 | s/mm | |||
| 18 | m/min |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | -- | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 20 | kJ/m² |
| 23°C, 局部断裂 | ISO 179/1eA | 70 | kJ/m² | |
| Notched Izod Impact Strength | -40°C | ISO 180/1A | 20 | kJ/m² |
| -30°C | ISO 180/1A | 15 | kJ/m² | |
| 23°C | ISO 180/1A | 80 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Oxygen Index | ISO 4589-2 | 20 | % | |
| Burning Rate | 1.00 mm | ISO 3795 | < 100 | mm/min |
| Flame Rating | 0.8 mm | UL 94, IEC 60695-11-10, -20 | HB | |
| 1.5 mm | UL 94, IEC 60695-11-10, -20 | HB | ||
| FMVSS Flammability | FMVSS 302 | B |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.