PA66 Zytel® ST801AHS BK010 DUPONT USA
85
- Unit Price:
- $5711 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 125.1MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance
- Application Areas:Home appliance components Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | Across Flow | ISO 294-4 | 1.4 | % |
| 流量 | ISO 294-4 | 1.8 | % | |
| Moisture Absorption | 24 hr, 23°C | ISO 62 | 1.1 | % |
| Saturation, 23°C, 2.00 mm | ISO 62 | 6.5 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | ISO 62 | 2.0 | % | |
| Viscosity number | ISO 307 | 130 | cm³/g | |
| Density | ISO 1183 | 1.07 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress | 50% Strain | ISO 527-2 | 49.0 | Mpa |
| Tensile Strain | Break | ISO 527-2 | > 50 | % |
| Tensile Creep Modulus | 1 hr | ISO 899-1 | -- | Mpa |
| 1000 hr | ISO 899-1 | -- | Mpa | |
| Tensile Modulus | ISO 527-2 | 2000 | Mpa | |
| Flexural Modulus | ISO 178 | 1800 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed | ISO 75-2/B | 157 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 63.0 | °C | |
| Linear thermal expansion coefficient | Flow : 23 to 55°C | ASTM E831 | 1.4E-4 | cm/cm/°C |
| Flow | ISO 11359-2 | 1.4E-4 | cm/cm/°C | |
| Flow : -40 to 23°C | ISO 11359-2 | 1.1E-4 | cm/cm/°C | |
| Flow : 55 to 160°C | ISO 11359-2 | 1.6E-4 | cm/cm/°C | |
| Across Flow : 23 to 55°C | ASTM E831 | 1.3E-4 | cm/cm/°C | |
| Across Flow | ISO 11359-2 | 1.3E-4 | cm/cm/°C | |
| Across Flow : -40 to 23°C | ISO 11359-2 | 1.1E-4 | cm/cm/°C | |
| Across Flow : 55 to 160°C | ISO 11359-2 | 1.3E-4 | cm/cm/°C | |
| Vicat Softening Temperature | ISO 306/B50 | 205 | °C | |
| Glass Transition Temperature | ISO 11357-2 | 75.0 | °C | |
| Melting Temperature | ISO 11357-3 | 262 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation Factor? | 100 Hz | IEC 62631-2-1 | 5.0E-3 | |
| 1 MHz | IEC 62631-2-1 | 0.010 | ||
| Dielectric Strength | IEC 60243-1 | 25 | KV/mm | |
| Relative Permittivity | 1 MHz | IEC 62631-2-1 | 3.30 | |
| 100 Hz | IEC 62631-2-1 | 3.50 | ||
| Comparative Tracking Index | IEC 60112 | 600 | V | |
| Surface Resistivity | IEC 62631-3-2 | -- | ohms | |
| Volume Resistivity | IEC 62631-3-1 | > 1.0E+13 | ohms·m |
| Fill Analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ejection Temperature | 190 | °C |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature | 80 | °C | ||
| Drying time - Hot air dryer | 2.0 到 4.0 | hr | ||
| Suggested Max Moisture | 0.20 | % | ||
| Processing (Melt) Temp | 280 到 300 | °C | ||
| Melt Temperature, Optimum | 290 | °C | ||
| Mold Temperature | 50 到 100 | °C | ||
| Mold Temperature, Optimum | 80 | °C | ||
| Holding Pressure | 50.0 到 100 | Mpa | ||
| Drying Recommended | yes | |||
| Hold Pressure Time | 4.00 | s/mm | ||
| Maximum Screw Tangential Speed | 18 | m/min |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | -- | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 20 | kJ/m² |
| 23°C, Partial Break | ISO 179/1eA | 70 | kJ/m² | |
| Notched Izod Impact Strength | -40°C | ISO 180/1A | 20 | kJ/m² |
| -30°C | ISO 180/1A | 15 | kJ/m² | |
| 23°C | ISO 180/1A | 80 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Oxygen Index | ISO 4589-2 | 20 | % | |
| Burning Rate | 1.00 mm | ISO 3795 | < 100 | mm/min |
| Flame Rating | 0.8 mm | UL 94, IEC 60695-11-10, -20 | HB | |
| 1.5 mm | UL 94, IEC 60695-11-10, -20 | HB | ||
| FMVSS Flammability | FMVSS 302 | B |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.