TPE Hytrel® 8238 DuPont, European Union
236
- Properties:High temperature resistan
- Usages:GearCable sheathWire and cableJointHose
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD | ISO294-4 | 1.6 | % |
| MD | ISO294-4 | 1.6 | % | |
| Moisture Absorption | 23°C,24hr | ISO62 | 0.30 | % |
| 饱和,23°C,2.00mm | ISO62 | 0.60 | % | |
| 平衡,23°C,2.00mm,50%RH | ISO62 | 0.20 | % | |
| MediumDensity | 1.13 | g/cm³ | ||
| SpecificHeatCapacityofMelt | 2150 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.15 | W/m/K | ||
| Melt Mass-Flow Rate | 240°C/2.16kg | ISO1133 | 13 | g/10min |
| Melt Volume flow Rate | 240°C/2.16kg | ISO1133 | 11.5 | cm3/10min |
| Density / Specific Gravity | ISO1183 | 1.28 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Nominal Tensile Strain at Break | ISO527-2 | 340 | % | |
| Tensile Stress | 屈服 | ISO527-2 | 38.0 | Mpa |
| 断裂 | ISO527-2 | 46.0 | Mpa | |
| 10%应变 | ISO527-2 | 34.0 | Mpa | |
| 50%应变 | ISO527-2 | 28.0 | Mpa | |
| 100%应变 | ISO527-2 | 26.0 | Mpa | |
| Tensile Strain | 屈服 | ISO527-2 | 19 | % |
| 断裂 | ISO527-2 | >300 | % | |
| Tensile Modulus | ISO527-2 | 1200 | Mpa | |
| Flexural Modulus | ISO178 | 1150 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,未退火 | ISO75-2/B | 105 | °C |
| 1.8MPa,未退火 | ISO75-2/A | 45.0 | °C | |
| Brittleness Temperature | ISO974 | -84.0 | °C | |
| Vicat Softening Temperature | -- | ISO306/A50 | 213 | °C |
| -- | ISO306/B50 | 150 | °C | |
| Linear thermal expansion coefficient | TD：-40to23°C | ISO11359-2 | 1E-04 | cm/cm/°C |
| TD：EffectiveThermalDiffusivity | ISO11359-2 | 5.44E-08 | m²/s | |
| MD：-- | ISO11359-2 | 1.5E-04 | cm/cm/°C | |
| MD：-40to23°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 1.4E-04 | cm/cm/°C | |
| Glass Transition Temperature | ISO11357-2 | 50.0 | °C | |
| Melting Temperature | ISO11357-3 | 221 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric Strength | IEC60243-1 | 21 | KV/mm | |
| Relative Permittivity | 100Hz | IEC60250 | 4.00 | |
| 1MHz | IEC60250 | 3.70 | ||
| Comparative Tracking Index | IEC60112 | 600 | V | |
| Surface Resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume Resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dissipation Factor? | 100Hz | IEC60250 | 0.010 | |
| 1MHz | IEC60250 | 0.018 |
| Elastomers Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tearing Strength | 横向流量 | ISO34-1 | 210 | kN/m |
| 流量 | ISO34-1 | 230 | kN/m |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -40°C | ISO179/1eA | 5.0 | kJ/m² |
| -30°C | ISO179/1eA | 5.0 | kJ/m² | |
| 23°C | ISO179/1eA | 15 | kJ/m² | |
| Notched Izod Impact Strength | -40°C | ISO180/1A | 5.5 | kJ/m² |
| 23°C | ISO180/1A | 11 | kJ/m² | |
| Tensile Impact Strength | 23°C | ISO8256/1 | 57.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore Hardness | 邵氏D | ISO868 | 76 | |
| 邵氏D,15秒 | ISO868 | 70 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.9mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.9mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| Oxygen Index | ISO4589-2 | 22 | % | |
| FMVSS Flammability | FMVSS302 | SE |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 550 | µgC/g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.