Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 1.8 | % |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD | ISO294-4 | 0.60 | % |
| Modeling Shrinkage | MD | ISO294-4 | 0.20 | % |
| Moisture Absorption | 饱和,23°C,2.00mm | ISO62 | 6.3 | % |
| Moisture Absorption | 平衡,23°C,2.00mm,50%RH | ISO62 | 1.9 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | 断裂 | ISO527-2 | 180 | Mpa |
| Tensile Strain | 断裂 | ISO527-2 | 3.5 | % |
| Tensile Modulus | | ASTM D638/ISO 527 | 9100 | kg/cm²(MPa)[Lb/in²] |
| Tensile Modulus | | ISO527-2 | 10000 | Mpa |
| Flexural Modulus | | ISO178 | 8500 | Mpa |
| Flexural Modulus | | ASTM D790/ISO 178 | 9000 | kg/cm²(MPa)[Lb/in²] |
| Compressive Stress | | ISO604 | 160 | Mpa |
| Shearing Strength | | ASTMD732 | 60.0 | Mpa |
| Flexural Stress | | ISO178 | 240 | Mpa |
| Charpy impact strength | | ASTM D256/ISO 179 | 6 | kg·cm/cm(J/M)ft·lb/in |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear thermal expansion coefficient | MD | ISO11359-2 | 1.4E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | TD | ISO11359-2 | 1E-04 | cm/cm/°C |
| Melting Temperature | | ISO11357-3 | 221 | °C |
| Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 221 | ℃（℉） |
| Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 210 | ℃（℉） |
| Deflection Temperature Under Load? | 0.45MPa,未退火 | ISO75-2/B | 220 | °C |
| Deflection Temperature Under Load? | 1.8MPa,未退火 | ISO75-2/A | 210 | °C |
| Melting Temperature | | | 221 | ℃（℉） |
| Vicat Softening Temperature | | ASTM D1525/ISO R306 | 215 | ℃（℉） |
| Glass Transition Temperature | | ISO11357-2 | 60.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation Factor? | 100Hz | IEC60250 | 0.022 | |
| Relative Permittivity | 100Hz | IEC60250 | 3.80 | |
| Comparative Tracking Index | | IEC60112 | 600 | V |
| Comparative Tracking Index | CTI | UL746 | PLC0 | |
| Volume Resistivity | | IEC60093 | 1E+14 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 80 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 90 | kJ/m² |
| Notched Izod impact strength | -30°C | ISO180/1U | 90 | kJ/m² |
| Notched Izod impact strength | 23°C | ISO180/1U | 100 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| UL flame retardant rating | 3.0mm | UL94 | HB | |
| UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB | |
| UL flame retardant rating | 3.0mm | IEC60695-11-10,-20 | HB | |
| Oxygen Index | | ISO4589-2 | 21 | % |
| FMVSS Flammability | | FMVSS302 | B | |
| atomization | F-value(refraction) | ISO6452 | 95 | % |
| atomization | G-value(condensate) | ISO6452 | 1E-04 | g |
| Burning Rate | 1.00mm | ISO3795 | 25 | mm/min |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|
| EmissionofOrganicCompounds | | VDA277 | 8.50 | µgC/g |
| Odor | | VDA270 | 3.50 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.