PA6 Zytel® 73G30L NC010 DUPONT USA

135

Unit Price:
$1673 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
52MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High temperature resistan enhance
Application Areas:auto parts Electronic appliances Home appliance accessorie
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption 23℃/24H		ASTM D570/ISO 62	1.8	%

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD	ISO294-4	0.60	%
Modeling Shrinkage	Modeling Shrinkage	MD	ISO294-4	0.20	%
Moisture Absorption	Saturation,23°C,2.00mm	ISO62	6.3	%
Moisture Absorption	Moisture Absorption	Equilibrium,23°C,2.00mm,50%RH	ISO62	1.9	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Stress	Break	ISO527-2	180	Mpa
Tensile Strain	Break	ISO527-2	3.5	%
Tensile Modulus		ASTM D638/ISO 527	9100	kg/cm²(MPa)[Lb/in²]
Tensile Modulus	Tensile Modulus		ISO527-2	10000	Mpa
Flexural Modulus		ASTM D790/ISO 178	9000	kg/cm²(MPa)[Lb/in²]
Flexural Modulus	Flexural Modulus		ISO178	8500	Mpa
Compressive Stress		ISO604	160	Mpa
Shearing Strength		ASTMD732	60.0	Mpa
Flexural Stress		ISO178	240	Mpa
Charpy impact strength		ASTM D256/ISO 179	6	kg·cm/cm(J/M)ft·lb/in

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Linear thermal expansion coefficient	MD	ISO11359-2	1.4E-05	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD	ISO11359-2	1E-04	cm/cm/°C
Melting Temperature		ISO11357-3	221	°C
Deflection Temperature Under Load?		ASTM D648/ISO 75	221	℃（℉）
	Deflection Temperature Under Load?		ASTM D648/ISO 75	210	℃（℉）
		Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	220	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	210	°C
Melting Temperature			221	℃（℉）
Vicat Softening Temperature		ASTM D1525/ISO R306	215	℃（℉）
Glass Transition Temperature		ISO11357-2	60.0	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dissipation Factor?	100Hz	IEC60250	0.022
Relative Permittivity	100Hz	IEC60250	3.80
Comparative Tracking Index		IEC60112	600	V
Comparative Tracking Index	CTI	UL746	PLC0
Volume Resistivity		IEC60093	1E+14	ohms·cm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	80	kJ/m²
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	90	kJ/m²
Notched Izod impact strength	-30°C	ISO180/1U	90	kJ/m²
Notched Izod impact strength	Notched Izod impact strength	23°C	ISO180/1U	100	kJ/m²

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5mm	UL94	HB
	UL flame retardant rating	3.0mm	UL94	HB
		UL flame retardant rating	1.5mm	IEC60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	3.0mm	IEC60695-11-10,-20	HB
Oxygen Index		ISO4589-2	21	%
FMVSS Flammability		FMVSS302	B
atomization	F-value(refraction)	ISO6452	95	%
atomization	atomization	G-value(condensate)	ISO6452	1E-04	g
Burning Rate	1.00mm	ISO3795	25	mm/min

Supplementary information	Test Condition	Test Method	Test Result	Unit
EmissionofOrganicCompounds		VDA277	8.50	µgC/g
Odor		VDA270	3.50

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.