Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Volume flow Rate | 260℃，5 kg 260℃/5.0 kg | ISO 1133 | 15 | cm3/10min |
| Apparent Density | | ISO 60 | 0.8 | g/cm³ |
| Modeling Shrinkage | TD：250℃，2.0 mm Across Flow : 482°F, 0.0787 in 2 2 | ISO 294-4 | 0.9 | % |
| Modeling Shrinkage | TD：120℃，2.0 mm，2 hrs Across Flow : 120°C, 2 hr, 2.00 mm 3 3 | ISO 294-4 | 0.5 | % |
| Modeling Shrinkage | MD：250℃，2.0 mm Flow : 482°F, 0.0787 in 2 2 | ISO 294-4 | 0.9 | % |
| Modeling Shrinkage | MD：120℃，2.0 mm，2 hrs Flow : 120°C, 2 hr, 2.00 mm 3 3 | ISO 294-4 | 0.5 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Modulus | 23℃ 23℃ 4 | ISO 178-A | 2500 | Mpa |
| Tensile Modulus | 23℃ 23℃ | ISO 527-1-2 | 2400 | Mpa |
| Flexural Strain | | | 5 | % |
| Nominal Tensile Strain at Break | 23℃ 23℃ | ISO 527-2/50 | > 15 | % |
| Flexural Strength | 3.50% 应变 3.5% Strain | ISO 178-A | 70 | Mpa |
| Flexural Strength | 23℃ 23°C | ISO 178 | 75 | Mpa |
| Ball Indentation Hardness | | ISO 2039-1 | 104 | Mpa |
| Tensile Strength | 屈服，23℃ 屈服，23℃ | ISO 527-2/50 | 45 | Mpa |
| Tensile Strain | 屈服，23℃ 屈服，23℃ | ISO 527-2/50 | 2.9 | % |
| Electrical | Test Condition | Test Method | Test Result | Unit |
|---|
| Relative Permittivity | 23℃，100 Hz 23°C, 100 Hz | IEC 60250 | 3.3 | |
| Relative Permittivity | 23℃，1 MHz 23°C, 1 MHz | IEC 60250 | 2.9 | |
| Dissipation Factor? | 23℃，100 Hz 23°C, 100 Hz | IEC 60250 | 0.025 | |
| Dissipation Factor? | 23℃，1 MHz 23°C, 1 MHz | IEC 60250 | 0.014 | |
| Comparative Tracking Index | 解决方案 A 解决方案 A | IEC 60112 | 300 | V |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Unnotched Izod Impact Strength | -30℃ -30°C | ISO 180/1U | 150 | kJ/m² |
| Unnotched Izod Impact Strength | 23℃ 23°C | ISO 180/1U | No Break | |
| Notched Izod Impact Strength | -30℃ -30°C | ISO 180-1A | < 10 | kJ/m² |
| Notched Izod Impact Strength | 0℃ 0°C | ISO 180-1A | 11 | kJ/m² |
| Notched Izod Impact Strength | 23℃ 23°C | ISO 180-1A | 10 | kJ/m² |
| Charpy Unnotched Impact Strength | -30℃ -30°C | ISO 179/1eU | 170 | kJ/m² |
| Charpy Unnotched Impact Strength | 23℃ 23°C | ISO 179/1eU | No Break | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating (0.75 mm) | 0.75 mm | UL 94 | V-0 | |
| Glow Wire Flammability Index | 0.80 mm 0.8 mm | IEC 60695-2-12 | 960 | °C |
| Glow Wire Ignition Temperature | 0.8 mm 0.8 mm | IEC 60695-2-13 | 800 | °C |
| Glow Wire Ignition Temperature | 1.6 mm 1.6 mm | IEC 60695-2-13 | 800 | °C |
| Glow Wire Ignition Temperature | 3 mm 3.0 mm | IEC 60695-2-13 | 800 | °C |
| Thermal | Test Condition | Test Method | Test Result | Unit |
|---|
| Coefficient of Linear Thermal Expansion | TD：23~55℃ TD：23 到 55℃ | ISO 11359-2 | 0.00010 | 1/℃ |
| Coefficient of Linear Thermal Expansion | MD：23~55℃ MD：23 到 55℃ | ISO 11359-2 | 0.000080 | 1/℃ |
| Heat Deflection Temperature | 1.8 MPa，未退火 1.8 MPa，未退火 | ISO 75-2/A | 75 | °C |
| Heat Deflection Temperature | 0.45 MPa，未退火 0.45 MPa，未退火 | ISO 75-2/B | 95 | °C |
| Vicat Softening Temperature | B120 B120 | ISO 306/B120 | 118 | °C |
| Ball Indentation Hardness | 115℃ 115℃ | IEC 60695-10-2 | Pass | |
| Melting temperature | | ISO 11357-3 | 225 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.