PC/PBT Pocan® DPCF2200 LANXESS GERMANY
92
- Unit Price:
- $3223 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 35MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Volume flow Rate | 260℃，5 kg 260℃/5.0 kg | ISO 1133 | 15 | cm3/10min |
| Apparent Density | ISO 60 | 0.8 | g/cm³ | |
| Modeling Shrinkage | TD：250℃，2.0 mm Across Flow : 482°F, 0.0787 in 2 2 | ISO 294-4 | 0.9 | % |
| TD：120℃，2.0 mm，2 hrs Across Flow : 120°C, 2 hr, 2.00 mm 3 3 | ISO 294-4 | 0.5 | % | |
| MD：250℃，2.0 mm Flow : 482°F, 0.0787 in 2 2 | ISO 294-4 | 0.9 | % | |
| MD：120℃，2.0 mm，2 hrs Flow : 120°C, 2 hr, 2.00 mm 3 3 | ISO 294-4 | 0.5 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Modulus | 23℃ 23℃ 4 | ISO 178-A | 2500 | Mpa |
| Tensile Modulus | 23℃ 23℃ | ISO 527-1-2 | 2400 | Mpa |
| Flexural Strain | 5 | % | ||
| Nominal Tensile Strain at Break | 23℃ 23℃ | ISO 527-2/50 | > 15 | % |
| Flexural Strength | 3.50% Strain 3.5% Strain | ISO 178-A | 70 | Mpa |
| 23℃ 23°C | ISO 178 | 75 | Mpa | |
| Ball Indentation Hardness | ISO 2039-1 | 104 | Mpa | |
| Tensile Strength | Yield，23℃ Yield，23℃ | ISO 527-2/50 | 45 | Mpa |
| Tensile Strain | Yield，23℃ Yield，23℃ | ISO 527-2/50 | 2.9 | % |
| Electrical | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative Permittivity | 23℃，100 Hz 23°C, 100 Hz | IEC 60250 | 3.3 | |
| 23℃，1 MHz 23°C, 1 MHz | IEC 60250 | 2.9 | ||
| Dissipation Factor? | 23℃，100 Hz 23°C, 100 Hz | IEC 60250 | 0.025 | |
| 23℃，1 MHz 23°C, 1 MHz | IEC 60250 | 0.014 | ||
| Comparative Tracking Index | Solution A Solution A | IEC 60112 | 300 | V |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Unnotched Izod Impact Strength | -30℃ -30°C | ISO 180/1U | 150 | kJ/m² |
| 23℃ 23°C | ISO 180/1U | No Break | ||
| Notched Izod Impact Strength | -30℃ -30°C | ISO 180-1A | < 10 | kJ/m² |
| 0℃ 0°C | ISO 180-1A | 11 | kJ/m² | |
| 23℃ 23°C | ISO 180-1A | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | -30℃ -30°C | ISO 179/1eU | 170 | kJ/m² |
| 23℃ 23°C | ISO 179/1eU | No Break |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame Rating (0.75 mm) | 0.75 mm | UL 94 | V-0 | |
| Glow Wire Flammability Index | 0.80 mm 0.8 mm | IEC 60695-2-12 | 960 | °C |
| Glow Wire Ignition Temperature | 0.8 mm 0.8 mm | IEC 60695-2-13 | 800 | °C |
| 1.6 mm 1.6 mm | IEC 60695-2-13 | 800 | °C | |
| 3 mm 3.0 mm | IEC 60695-2-13 | 800 | °C |
| Thermal | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Coefficient of Linear Thermal Expansion | TD：23~55℃ TD：23 to 55℃ | ISO 11359-2 | 0.00010 | 1/℃ |
| MD：23~55℃ MD：23 to 55℃ | ISO 11359-2 | 0.000080 | 1/℃ | |
| Heat Deflection Temperature | 1.8 MPa，Unannealed 1.8 MPa，Unannealed | ISO 75-2/A | 75 | °C |
| 0.45 MPa，Unannealed 0.45 MPa，Unannealed | ISO 75-2/B | 95 | °C | |
| Vicat Softening Temperature | B120 B120 | ISO 306/B120 | 118 | °C |
| Ball Indentation Hardness | 115℃ 115℃ | IEC 60695-10-2 | Pass | |
| Melting temperature | ISO 11357-3 | 225 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.