Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | 流动 : 1.50 到 3.20 mm | 内部方法 | 0.30 到 0.50 | % |
| Modeling Shrinkage | 流动 : 3.20 到 4.60 mm | 内部方法 | 0.50 到 0.80 | % |
| Modeling Shrinkage | 横向流动 : 1.50 到 3.20 mm | 内部方法 | 0.40 到 0.60 | % |
| Modeling Shrinkage | 横向流动 : 3.20 到 4.60 mm | 内部方法 | 0.60 到 0.90 | % |
| Moisture Absorption | 24 hr | ASTM D570 | 0.060 | % |
| Specific Volume | | ASTM D792 | 0.660 | cm³/g |
| Outdoor Suitability | | UL 746C | f2 | |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Modulus | 50.0 mm 跨距 | ASTM D790 | 6890 | Mpa |
| Flexural Strength | 断裂, 50.0 mm 跨距 | ASTM D790 | 189 | Mpa |
| Tensile Strength | 断裂 | ASTM D638 | 110 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| RTI | | UL 746 | 125 | °C |
| RTI Imp | | UL 746 | 110 | °C |
| RTI Elec | | UL 746 | 125 | °C |
| Coefficient of Linear Thermal Expansion (Flow) | -40 到 40°C | ASTM E831 | 2.3E-5 | cm/cm/°C |
| Coefficient of Linear Thermal Expansion (Flow) | 60 到 138°C | ASTM E831 | 1.6E-5 | cm/cm/°C |
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 215 | °C |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 176 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Comparative Tracking Index | | UL 746 | PLC 4 | |
| Hot-wire Ignition | | UL 746 | PLC 1 | |
| High Amp Arc Ignition | | UL 746 | PLC 3 | |
| Dielectric Constant | 100 Hz | ASTM D150 | 3.60 | |
| Dielectric Constant | 1 MHz | ASTM D150 | 3.60 | |
| Volume Resistivity | | ASTM D257 | 5.9E+16 | ohms·cm |
| Dissipation Factor? | 100 Hz | ASTM D150 | 1.4E-3 | |
| Dissipation Factor? | 1 MHz | ASTM D150 | 0.020 | |
| Dielectric Strength | 1.60 mm, in Oil | ASTM D149 | 29 | KV/mm |
| Dielectric Strength | 3.20 mm, in Air | ASTM D149 | 24 | KV/mm |
| High Voltage Arc Tracking Rate | | UL 746 | PLC 2 | |
| Arc Resistance | | ASTM D495 | PLC 6 | |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|
| Drying Temperature | | | 120 | °C |
| Suggested Max Moisture | | | 0.020 | % |
| Processing (Melt) Temp | | | 250 到 265 | °C |
| Mold Temperature | | | 65 到 90 | °C |
| Drying Time | | | 3.0 到 4.0 | hr |
| Suggested Shot Size | | | 40 到 80 | % |
| Rear Temperature | | | 240 到 255 | °C |
| Middle Temperature | | | 245 到 260 | °C |
| Front Temperature | | | 250 到 265 | °C |
| Nozzle Temperature | | | 245 到 260 | °C |
| Back Pressure | | | 0.300 到 0.700 | Mpa |
| Screw Speed | | | 50 到 80 | rpm |
| Vent Depth | | | 0.025 到 0.038 | mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Instrumented Dart Impact | 23°C, Energy at Peak | ASTM D3763 | 6.00 | J |
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 8.00 | J |
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 640 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R 级 | ASTM D785 | 119 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | 1.5 mm | UL 94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.