Material Description

Technical Data Sheet

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow : 1.50 to 3.20 mm	内部方法	0.30 到 0.50	%
	Modeling Shrinkage	Flow : 3.20 to 4.60 mm	内部方法	0.50 到 0.80	%
		Modeling Shrinkage	Across Flow : 1.50 to 3.20 mm	内部方法	0.40 到 0.60	%
		Modeling Shrinkage	Modeling Shrinkage	Across Flow : 3.20 to 4.60 mm	内部方法	0.60 到 0.90	%
Moisture Absorption	24 hr	ASTM D570	0.060	%
Specific Volume		ASTM D792	0.660	cm³/g
Outdoor Suitability		UL 746C	f2

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Modulus	50.0 mm Span	ASTM D790	6890	Mpa
Flexural Strength	Break, 50.0 mm Span	ASTM D790	189	Mpa
Tensile Strength	Break	ASTM D638	110	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
RTI		UL 746	125	°C
RTI Imp		UL 746	110	°C
RTI Elec		UL 746	125	°C
Coefficient of Linear Thermal Expansion (Flow)	-40 to 40°C	ASTM E831	2.3E-5	cm/cm/°C
Coefficient of Linear Thermal Expansion (Flow)	Coefficient of Linear Thermal Expansion (Flow)	60 to 138°C	ASTM E831	1.6E-5	cm/cm/°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	215	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	176	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index		UL 746	PLC 4
Hot-wire Ignition		UL 746	PLC 1
High Amp Arc Ignition		UL 746	PLC 3
Dielectric Constant	100 Hz	ASTM D150	3.60
Dielectric Constant	Dielectric Constant	1 MHz	ASTM D150	3.60
Volume Resistivity		ASTM D257	5.9E+16	ohms·cm
Dissipation Factor?	100 Hz	ASTM D150	1.4E-3
Dissipation Factor?	Dissipation Factor?	1 MHz	ASTM D150	0.020
Dielectric Strength	1.60 mm, in Oil	ASTM D149	29	KV/mm
Dielectric Strength	Dielectric Strength	3.20 mm, in Air	ASTM D149	24	KV/mm
High Voltage Arc Tracking Rate		UL 746	PLC 2
Arc Resistance		ASTM D495	PLC 6

Injection	Test Result	Unit
Drying Temperature	120	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	250 到 265	°C
Mold Temperature	65 到 90	°C
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	40 到 80	%
Rear Temperature	240 到 255	°C
Middle Temperature	245 到 260	°C
Front Temperature	250 到 265	°C
Nozzle Temperature	245 到 260	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	50 到 80	rpm
Vent Depth	0.025 到 0.038	mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C, Energy at Peak	ASTM D3763	6.00	J
Instrumented Dart Impact	Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	8.00	J
Unnotched Izod Impact Strength	23°C	ASTM D4812	640	J/m

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Scale	ASTM D785	119

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	1.5 mm	UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.