Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | 24hr | ASTMD570 | 0.10 | % |
Melt Mass-Flow Rate | 400°C/2.16kg | ASTMD1238 | 11 | g/10min |
Modeling Shrinkage | MD:3.18mm | ASTMD955 | 0.0到0.20 | % |
Modeling Shrinkage | TD:3.18mm | ASTMD955 | 1.4到1.6 | % |
Density / Specific Gravity | | ASTMD792 | 1.41 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Compressive Strength | | ASTMD695 | 188 | Mpa |
Shearing Strength | | ASTMD732 | 103 | Mpa |
Tensile Stress | -- | ASTMD638 | 223 | Mpa |
Tensile Stress | 屈服 | ISO527-2/1A/5 | 218 | Mpa |
Tensile Modulus | -- | ASTMD638 | 20900 | Mpa |
Tensile Modulus | -- | ISO527-2/1A/1 | 25400 | Mpa |
Tensile Elongation | 断裂5 | ASTMD638 | 1.7 | % |
Tensile Elongation | 断裂 | ISO527-2/1A/5 | 1.7 | % |
Flexural Modulus | -- | ASTMD790 | 17900 | Mpa |
Flexural Modulus | -- | ISO178 | 21500 | Mpa |
Flexural Strength | -- | ASTMD790 | 321 | Mpa |
Flexural Strength | -- | ISO178 | 319 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.8MPa,退火 | ASTMD648 | 315 | °C |
Linear thermal expansion coefficient | MD:-50到50°C | ASTME831 | 6.7E-06 | cm/cm/°C |
Peak Melting Temperature | | ASTMD3418 | 343 | °C |
Glass Transition Temperature | | ASTMD3418 | 147 | °C |
Specific Heat | 50°C | DSC | 1310 | J/kg/°C |
Specific Heat | 200°C | DSC | 1810 | J/kg/°C |
Thermal Conductivity | | ASTMC177 | 0.37 | W/m/K |
Fill Analysis | Test Condition | Test Method | Test Result | Unit |
---|
Melt Viscosity | 400°C,1000sec^-1 | ASTMD3835 | 450 | Pa·s |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Unnotched Izod Impact Strength | -- | ASTMD4812 | 640 | J/m |
Unnotched Izod Impact Strength | -- | ISO180 | 43 | kJ/m² |
Notched Izod Impact Strength | -- | ASTMD256 | 64 | J/m |
Notched Izod Impact Strength | -- | ISO180 | 8.5 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | M级 | ASTMD785 | 106 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 0.8mm | UL94 | V-0 | |
UL flame retardant rating | 1.6mm | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.