PEEK KetaSpire® KT-880 CF30 SOLVAY USA
180
- Unit Price:
- $80894 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 26MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Chemical resistance Fatigue resistance heat-resisting Glass fiber reinforced
- Application Areas:Electrical field Electronic field Industrial applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | 24hr | ASTMD570 | 0.10 | % |
| Melt Mass-Flow Rate | 400°C/2.16kg | ASTMD1238 | 11 | g/10min |
| Modeling Shrinkage | MD:3.18mm | ASTMD955 | 0.0到0.20 | % |
| TD:3.18mm | ASTMD955 | 1.4到1.6 | % | |
| Density / Specific Gravity | ASTMD792 | 1.41 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compressive Strength | ASTMD695 | 188 | Mpa | |
| Shearing Strength | ASTMD732 | 103 | Mpa | |
| Tensile Stress | -- | ASTMD638 | 223 | Mpa |
| Yield | ISO527-2/1A/5 | 218 | Mpa | |
| Tensile Modulus | -- | ASTMD638 | 20900 | Mpa |
| -- | ISO527-2/1A/1 | 25400 | Mpa | |
| Tensile Elongation | Break5 | ASTMD638 | 1.7 | % |
| Break | ISO527-2/1A/5 | 1.7 | % | |
| Flexural Modulus | -- | ASTMD790 | 17900 | Mpa |
| -- | ISO178 | 21500 | Mpa | |
| Flexural Strength | -- | ASTMD790 | 321 | Mpa |
| -- | ISO178 | 319 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 1.8MPa,Annealed | ASTMD648 | 315 | °C |
| Linear thermal expansion coefficient | MD：-50to50°C | ASTME831 | 6.7E-06 | cm/cm/°C |
| Peak Melting Temperature | ASTMD3418 | 343 | °C | |
| Glass Transition Temperature | ASTMD3418 | 147 | °C | |
| Specific Heat | 50°C | DSC | 1310 | J/kg/°C |
| 200°C | DSC | 1810 | J/kg/°C | |
| Thermal Conductivity | ASTMC177 | 0.37 | W/m/K |
| Fill Analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Viscosity | 400°C,1000sec^-1 | ASTMD3835 | 450 | Pa·s |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Unnotched Izod Impact Strength | -- | ASTMD4812 | 640 | J/m |
| -- | ISO180 | 43 | kJ/m² | |
| Notched Izod Impact Strength | -- | ASTMD256 | 64 | J/m |
| -- | ISO180 | 8.5 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | M-Scale | ASTMD785 | 106 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL94 | V-0 | |
| 1.6mm | UL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.