Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 饱和,23°C | ISO62 | 0.45 | % |
| Melt Viscosity | 400°C | ISO11443 | 90.0 | Pa·s |
| Moisture Absorption | 100°C | ISO62 | 0.55 | % |
| Spiral Flow | --4 | 内部方法 | 24.5 | CM |
| Spiral Flow | --5 | 内部方法 | 28.0 | CM |
| Spiral Flow | --6 | 内部方法 | 33.0 | CM |
| Modeling Shrinkage | TD | ISO294-4 | 1.3 | % |
| Modeling Shrinkage | MD | ISO294-4 | 1.0 | % |
| Density / Specific Gravity | | ISO1183 | 1.30 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Compressive Stress | 23°C | ISO604 | 130 | Mpa |
| Compressive Stress | 120°C | ISO604 | 80.0 | Mpa |
| Tensile Stress | 屈服,23°C | ISO527-2 | 105 | Mpa |
| Tensile Strain | 断裂,23°C | ISO527-2 | 20 | % |
| Tensile Modulus | 23°C | ISO527-2 | 4100 | Mpa |
| Flexural Modulus | 23°C | ISO178 | 3900 | Mpa |
| Flexural Stress | 3.5%Strain,23°C | ISO178 | 130 | Mpa |
| Flexural Stress | 23°C8 | ISO178 | 175 | Mpa |
| Flexural Stress | 125°C | ISO178 | 90.0 | Mpa |
| Flexural Stress | 175°C | ISO178 | 20.0 | Mpa |
| Flexural Stress | 275°C | ISO178 | 13.5 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear thermal expansion coefficient | MD：<143°C | ISO11359-2 | 5E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | MD：>143°C | ISO11359-2 | 1.2E-04 | cm/cm/°C |
| Linear thermal expansion coefficient | TD：<143°C | ISO11359-2 | 5.5E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | TD：>143°C | ISO11359-2 | 1.4E-04 | cm/cm/°C |
| Melting temperature | | ISO11357-3 | 343 | °C |
| Deflection Temperature Under Load? | 1.8MPa,未退火 | ISO75-2/Af | 156 | °C |
| Thermal Conductivity | 23°C11 | ISO22007-4 | 0.29 | W/m/K |
| Thermal Conductivity | 23°C12 | ISO22007-4 | 0.32 | W/m/K |
| | ISO11357 | 143 | °C |
| Heat Deflection Temperature | 1.8MPa,Annealed | ISO75-2/Af | 167 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Electric strength | 2.50mm | IEC60243-1 | 23 | KV/mm |
| Dissipation Factor? | 23°C,1MHz | IEC60250 | 4E-03 | |
| Comparative Tracking Index | | IEC60112 | 150 | V |
| Dielectric Constant | 23°C,1kHz | IEC60250 | 3.10 | |
| Volume Resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
| Volume Resistivity | 125°C | IEC60093 | 1E+15 | ohms·cm |
| Volume Resistivity | 275°C | IEC60093 | 1E+09 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179 | NoBreak | |
| Notched Izod impact strength | 23°C | ISO180 | NoBreak | |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 4.0 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/A | 4.5 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | 邵氏D,23°C | ISO868 | 85 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Glow Wire Flammability Index | 2.0mm | IEC60695-2-12 | 960 | °C |
| Oxygen Index | --13 | ISO4589-2 | 24 | % |
| Oxygen Index | --14 | ISO4589-2 | 35 | % |
| Toxicity | COcontent | NES713 | 0.0740 | |
| Toxicity | CO2content | NES713 | 0.150 | |
| Toxicity | Totalgases | NES713 | 0.220 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.