PEEK VICTREX® 90G VICTREX UK

106

Unit Price:
$50691 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
39MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
MeltViscosity	400°C	ISO11443	90.0	Pa·s
Density/specific gravity 3		ISO1183	1.30	g/cm³
SpiralFlow3	--4	内部方法	24.5	CM
	SpiralFlow3	--5	内部方法	28.0	CM
	SpiralFlow3	SpiralFlow3	--6	内部方法	33.0	CM
Shrinkage rate 7	TD	ISO294-4	1.3	%
Shrinkage rate 7	Shrinkage rate 7	MD	ISO294-4	1.0	%
Water absorption rate	Saturation,23°C	ISO62	0.45	%
Water absorption rate - saturation	100°C	ISO62	0.55	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	23°C	ISO527-2	4100	Mpa
Tensile stress	Yield,23°C	ISO527-2	105	Mpa
Tensile strain	Break,23°C	ISO527-2	20	%
Bending modulus	23°C	ISO178	3900	Mpa
Bending stress	3.5%Strain,23°C	ISO178	130	Mpa
	Bending stress	23°C8	ISO178	175	Mpa
		Bending stress	125°C	ISO178	90.0	Mpa
			Bending stress	175°C	ISO178	20.0	Mpa
			Bending stress	Bending stress	275°C	ISO178	13.5	Mpa
Compressive stress	23°C	ISO604	130	Mpa
Compressive stress	Compressive stress	120°C	ISO604	80.0	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Linear coefficient of thermal expansion	MD：>143°C	ISO11359-2	1.2E-04	cm/cm/°C
	Linear coefficient of thermal expansion	TD：<143°C	ISO11359-2	5.5E-05	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：>143°C	ISO11359-2	1.4E-04	cm/cm/°C
thermal conductivity	23°C11	ISO22007-4	0.29	W/m/K
thermal conductivity	thermal conductivity	23°C12	ISO22007-4	0.32	W/m/K
Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/Af	156	°C
Hot deformation temperature 9	1.8MPa,Annealed	ISO75-2/Af	167	°C
GlassTransitionTemperature10		ISO11357	143	°C
Melting temperature		ISO11357-3	343	°C
Linear coefficient of thermal expansion	MD：<143°C	ISO11359-2	5E-05	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistivity	23°C	IEC60093	1E+16	ohms·cm
	Volume resistivity	125°C	IEC60093	1E+15	ohms·cm
	Volume resistivity	Volume resistivity	275°C	IEC60093	1E+09	ohms·cm
Electrical strength	2.50mm	IEC60243-1	23	KV/mm
Dielectric constant	23°C,1kHz	IEC60250	3.10
Dissipation factor	23°C,1MHz	IEC60250	4E-03
Leakage Trace Index		IEC60112	150	V

Impact performance	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	23°C	ISO179/1eA	4.0	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO179	NoBreak
Impact strength of cantilever beam gap	23°C	ISO180/A	4.5	kJ/m²
Unscented Izod impact strength	23°C	ISO180	NoBreak

hardness	Test Condition	Test Method	Test Result	Unit
Shore hardness	Shore D,23°C	ISO868	85

flammability	Test Condition	Test Method	Test Result	Unit
Burning wire flammability index	2.0mm	IEC60695-2-12	960	°C
Extreme Oxygen Index	--13	ISO4589-2	24	%
Extreme Oxygen Index	Extreme Oxygen Index	--14	ISO4589-2	35	%
toxicity	COcontent	NES713	0.0740
	toxicity	CO2content	NES713	0.150
	toxicity	toxicity	Totalgases	NES713	0.220

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.