PBT VALOX™ 310SE0 SABIC INNOVATIVE US
202
- Properties:Flame retardant
- Usages:Electrical fieldElectronic fieldHome appliance componentsswitchShellSpool
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：--2 | 内部方法 | 1.1to1.8 | % |
| MD：--3 | 内部方法 | 1.5to2.3 | % | |
| MD：--4 | 内部方法 | 0.90to1.6 | % | |
| MD：3.20mm | 内部方法 | 1.5to2.3 | % | |
| TD：--2 | 内部方法 | 0.90to1.9 | % | |
| TD：--4 | 内部方法 | 1.0to1.7 | % | |
| TD：--3 | 内部方法 | 1.6to2.4 | % | |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.36 | % |
| 平衡,23°C,50%RH | ISO62 | 0.080 | % | |
| Melt Mass-Flow Rate | 250°C/2.16kg | ASTMD1238 | 8.6 | g/10min |
| Melt Volume flow Rate | 250°C/2.16kg | ISO1133 | 8.00 | cm3/10min |
| Density / Specific Gravity | ISO1183 | 1.40 | g/cm³ | |
| ASTMD792 | 1.40 | g/cm³ | ||
| Specific Volume | ASTMD792 | 0.710 | cm³/g |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 2620 | Mpa |
| Flexural Strength | ISO178 | 90.0 | Mpa | |
| Tensile Strain | Yield | ASTMD638 | 20 | % |
| Flexural Modulus | ISO178 | 2600 | Mpa | |
| Tensile Strength | Break | ASTMD638 | 58.0 | Mpa |
| Yield | ASTMD638 | 58.0 | Mpa | |
| Tensile Elongation | 断裂 | ASTMD638 | 20 | % |
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 101 | Mpa |
| Tensile Modulus | ASTMD638 | 2820 | Mpa | |
| Taber Abrasion Resistance | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 19.0 | mg |
| Tensile Stress | 屈服 | ISO527-2/50 | 55.0 | Mpa |
| 断裂 | ISO527-2/50 | 40.0 | Mpa | |
| Tensile Strain | 屈服 | ISO527-2/50 | 6.0 | % |
| 断裂 | ISO527-2/50 | 20 | % | |
| Tensile Modulus | ISO527-2/1 | 2800 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 1.8MPa,未退火,100mm跨距12 | ISO75-2/Ae | 60.0 | °C |
| 1.8MPa,未退火,64.0mm跨距13 | ISO75-2/Af | 71.0 | °C | |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 74.0 | °C | |
| 1.8MPa,未退火,6.40mm | ASTMD648 | 71.0 | °C | |
| 0.45MPa,未退火,6.40mm | ASTMD648 | 162 | °C | |
| Linear thermal expansion coefficient | MD：23to60°C | ISO11359-2 | 1E-04 | cm/cm/°C |
| TD：-40到40°C | ASTME831 | 7.9E-05 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 7.3E-05 | cm/cm/°C | |
| TD：23to60°C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| MD：-40to40°C | ASTME831 | 7.9E-05 | cm/cm/°C | |
| MD：60to138°C | ASTME831 | 1.3E-04 | cm/cm/°C | |
| MD：-40to40°C | ISO11359-2 | 7.6E-05 | cm/cm/°C | |
| RTIElec | UL746 | 120 | °C | |
| Evolution Calendar intelligent importer | UL746 | 120 | °C | |
| RTIStr | UL746 | 140 | °C | |
| Thermal Conductivity | ISO8302 | 0.24 | W/m/K | |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass | |
| Vicat Softening Temperature | ASTMD152514 | 165 | °C | |
| -- | ISO306/A50 | 212 | °C | |
| -- | ISO306/B50 | 165 | °C | |
| -- | ISO306/B120 | 165 | °C | |
| Heat Deflection Temperature | 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 135 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| High Amp Arc Ignition | HAI | UL746 | PLC0 | |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC4 | |
| High Amp Arc Ignition | PLC | UL746 | PLC6 | |
| Comparative Tracking Index | CTI | UL746 | PLC3 | |
| Hot-wire Ignition | HWI | UL746 | PLC2 | |
| Arc Resistance | ASTMD495 | PLC6 | ||
| Relative Permittivity | 50Hz | IEC60250 | 2.90 | |
| 60Hz | IEC60250 | 2.90 | ||
| 100Hz | IEC60250 | 3.10 | ||
| 1MHz | IEC60250 | 2.80 | ||
| Comparative Tracking Index | -- | IEC60112 | 175 | V |
| 解决方案B | IEC60112 | 100 | V | |
| Dissipation Factor? | 50Hz | IEC60250 | 1E-03 | |
| 60Hz | IEC60250 | 1E-03 | ||
| 100Hz | IEC60250 | 2E-03 | ||
| 1MHz | IEC60250 | 0.010 | ||
| Dielectric Strength | 1.60mm,在油中 | ASTMD149 | 22 | KV/mm |
| 3.20mm,inAir | ASTMD149 | 18 | KV/mm | |
| 0.800mm,在油中 | IEC60243-1 | 31 | KV/mm | |
| 1.00mm15 | IEC60243-1 | 18 | KV/mm | |
| 1.60mm,在油中 | IEC60243-1 | 24 | KV/mm | |
| 3.20mm,在油中 | IEC60243-1 | 15 | KV/mm | |
| Surface Resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume Resistivity | IEC60093 | >1.0E+15 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 200 | J |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 3.0 | kJ/m² |
| 23°C | ISO180/1A | 5.0 | kJ/m² | |
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | NoBreak | |
| 23°C | ISO180/1U | NoBreak | ||
| Charpy Notched Impact Strength | 23°C10 | ISO179/1eA | 8.0 | kJ/m² |
| 23°C | ISO179/2C | 4.0 | kJ/m² | |
| -30°C10 | ISO179/1eA | 4.0 | kJ/m² | |
| Notched Izod Impact Strength | -30°C | ASTMD256 | 22 | J/m |
| 23°C | ASTMD256 | 37 | J/m | |
| 23°C | ASTMD4812 | 1600 | J/m | |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R级 | ISO2039-2 | 120 | |
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 105 | Mpa |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.71mm | UL94 | V-0 | |
| 3.0mm | UL94 | 5VA | ||
| Glow Wire Flammability Index | 1.0mm | IEC60695-2-12 | 960 | °C |
| Oxygen Index | ISO4589-2 | 30 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.