Density / Specific Gravity

ASTMD792

g/cm³

1

Density / Specific Gravity

ISO1183

g/cm³

1

Melt Volume flow Rate

250°C/2.16kg

ISO1133

cm3/10min

8

Melt Mass-Flow Rate

250°C/2.16kg

ASTMD1238

g/10min

8

Modeling Shrinkage

MD：--2

内部方法

%

1

Modeling Shrinkage

MD：--3

内部方法

%

1

Modeling Shrinkage

MD：--4

内部方法

%

0

Modeling Shrinkage

MD：3.20mm

内部方法

%

1

Modeling Shrinkage

TD：--2

内部方法

%

0

Modeling Shrinkage

TD：--4

内部方法

%

1

Modeling Shrinkage

TD：--3

内部方法

%

1

Specific Volume

ASTMD792

cm³/g

0

Moisture Absorption

饱和,23°C

ISO62

%

0

Moisture Absorption

平衡,23°C,50%RH

ISO62

%

0

Flexural Strength

Yield,50.0mmSpan

ASTMD790

Mpa

1

Tensile Modulus

ISO527-2/1

Mpa

2

Tensile Modulus

ASTMD638

Mpa

2

Tensile Strength

Break

ASTMD638

Mpa

5

Tensile Strength

Yield

ASTMD638

Mpa

5

Tensile Strain

屈服

ISO527-2/50

%

6

Tensile Strain

断裂

ISO527-2/50

%

2

Tensile Strain

Yield

ASTMD638

%

2

Tensile Stress

屈服

ISO527-2/50

Mpa

5

Tensile Stress

断裂

ISO527-2/50

Mpa

4

Tensile Elongation

断裂

ASTMD638

%

2

Taber Abrasion Resistance

1000Cycles,1000g,CS-17转轮

内部方法

mg

1

Flexural Modulus

50.0mmSpan

ASTMD790

Mpa

2

Flexural Modulus

ISO178

Mpa

2

Flexural Strength

ISO178

Mpa

9

RTIElec

UL746

°C

1

Evolution Calendar intelligent importer

UL746

°C

1

RTIStr

UL746

°C

1

Thermal Conductivity

ISO8302

W/m/K

0

Deflection Temperature Under Load?

1.8MPa,未退火,3.20mm

ASTMD648

°C

7

Deflection Temperature Under Load?

1.8MPa,未退火,6.40mm

ASTMD648

°C

7

Deflection Temperature Under Load?

0.45MPa,未退火,6.40mm

ASTMD648

°C

1

Deflection Temperature Under Load?

1.8MPa,未退火,100mm跨距12

ISO75-2/Ae

°C

6

Deflection Temperature Under Load?

1.8MPa,未退火,64.0mm跨距13

ISO75-2/Af

°C

7

Heat Deflection Temperature

0.45MPa,Unannealed,100mmSpan

ISO75-2/Be

°C

1

Vicat Softening Temperature

ASTMD152514

°C

1

Vicat Softening Temperature

--

ISO306/A50

°C

2

Vicat Softening Temperature

--

ISO306/B50

°C

1

Vicat Softening Temperature

--

ISO306/B120

°C

1

Linear thermal expansion coefficient

MD：23to60°C

ISO11359-2

cm/cm/°C

1

Linear thermal expansion coefficient

TD：-40到40°C

ASTME831

cm/cm/°C

7

Linear thermal expansion coefficient

TD：-40to40°C

ISO11359-2

cm/cm/°C

7

Linear thermal expansion coefficient

TD：23to60°C

ISO11359-2

cm/cm/°C

1

Linear thermal expansion coefficient

MD：-40to40°C

ASTME831

cm/cm/°C

7

Linear thermal expansion coefficient

MD：60to138°C

ASTME831

cm/cm/°C

1

Linear thermal expansion coefficient

MD：-40to40°C

ISO11359-2

cm/cm/°C

7

Surface Resistivity

IEC60093

ohms

>

Dielectric Strength

1.60mm,在油中

ASTMD149

KV/mm

2

Dielectric Strength

3.20mm,inAir

ASTMD149

KV/mm

1

Dielectric Strength

0.800mm,在油中

IEC60243-1

KV/mm

3

Dielectric Strength

1.00mm15

IEC60243-1

KV/mm

1

Dielectric Strength

1.60mm,在油中

IEC60243-1

KV/mm

2

Dielectric Strength

3.20mm,在油中

IEC60243-1

KV/mm

1

Comparative Tracking Index

--

IEC60112

V

1

Comparative Tracking Index

解决方案B

IEC60112

V

1

Volume Resistivity

IEC60093

ohms·cm

>

Charpy Notched Impact Strength

-30°C10

ISO179/1eA

kJ/m²

4

Charpy Notched Impact Strength

23°C10

ISO179/1eA

kJ/m²

8

Charpy Notched Impact Strength

23°C

ISO179/2C

kJ/m²

4

Notched Izod Impact Strength

23°C

ASTMD4812

J/m

1

Notched Izod Impact Strength

-30°C

ASTMD256

J/m

2

Notched Izod Impact Strength

23°C

ASTMD256

J/m

3

Notched Izod Impact Strength

-30°C

ISO180/1A

kJ/m²

3

Notched Izod Impact Strength

23°C

ISO180/1A

kJ/m²

5

Instrumented Dart Impact

23°C,TotalEnergy

ASTMD3763

J

2

Ball Indentation Hardness

H358/30

ISO2039-1

Mpa

1

Oxygen Index

ISO4589-2

%

3

Glow Wire Flammability Index

1.0mm

IEC60695-2-12

°C

9