Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D792/ISO 1183 | 1.67 | |
| Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.020 | % |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | 横向流量 | 内部方法 | 0.60 | % |
| Modeling Shrinkage | 流量 | 内部方法 | 0.20 | % |
| Moisture Absorption | 饱和 | ASTM D570 | 0.020 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength | | ASTM D638 | 157 | Mpa |
| Tensile Elongation | 断裂 | ASTM D638 | 5.1 | % |
| Flexural Modulus | 23°C | ASTM D790 | 11800 | Mpa |
| Flexural Modulus | | ASTM D790/ISO 178 | 11800 | kg/cm²(MPa)[Lb/in²] |
| Flexural Strength | | ASTM D790/ISO 178 | 158 | kg/cm²(MPa)[Lb/in²] |
| Flexural Strength | 23°C | ASTM D790 | 158 | Mpa |
| Tensile Elongation?(Break) | | ASTM D638/ISO 527 | 5.1 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 269 | ℃（℉） |
| Linear thermal expansion coefficient | 流动 : 150°C | 内部方法 | 2.0E-6 | cm/cm/°C |
| Linear thermal expansion coefficient | 横向 : 150°C | 内部方法 | 8.5E-5 | cm/cm/°C |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火 | ASTM D648 | 269 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation Factor? | 1 MHz | ASTM D150 | 0.026 | |
| Dissipation Factor? | 1.00 GHz | ASTM D150 | 4.0E-3 | |
| Comparative Tracking Index | | IEC 60112 | 175 | V |
| Dielectric Constant | 1 MHz | ASTM D150 | 3.80 | |
| Dielectric Constant | 1.00 GHz | ASTM D150 | 3.50 | |
| Arc Resistance | | ASTM D495 | 124 | sec |
| Volume Resistivity | | ASTM D257 | 1.0E+15 | ohms·cm |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|
| Drying Temperature | | | 130 | °C |
| Processing (Melt) Temp | | | 350 | °C |
| Mold Temperature | | | 40 到 160 | °C |
| Holding Pressure | | | 20.0 到 40.0 | Mpa |
| Drying Time | | | 4.0 到 24 | hr |
| Rear Temperature | | | 280 到 320 | °C |
| Middle Temperature | | | 320 到 340 | °C |
| Front Temperature | | | 340 到 360 | °C |
| Nozzle Temperature | | | 340 到 360 | °C |
| Back Pressure | | | 1.00 到 5.00 | Mpa |
| Screw Speed | | | 50 到 100 | rpm |
| Injection Pressure | | | 80.0 到 160 | Mpa |
| Injection Rate | | | 中等偏快 | |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Unnotched Izod Impact Strength | 6.40 mm | ASTM D256 | 250 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R 级 | ASTM D785 | 106 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Oxygen Index | | ISO 527-1,-2(JIS K7161,7162) | 40 | % |
| Flame Rating | 0.30 mm, ALL | UL 94 | V-0 | |
| | 内部方法 | 300 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices