Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LCP E6007LHF SUMITOMO JAPAN
SUMIKASUPER®
Automotive sector
Low warpage、Good forming performance、Glass fiber reinforced、enhance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical Properties
Test Condition
Test Method
Unit
LCP/SUMITOMO JAPAN/E6007LHF
Moisture Absorption 23℃/24H
ASTM D570/ISO 62
%
0
Physical Properties
Test Condition
Test Method
Unit
LCP/SUMITOMO JAPAN/E6007LHF
Modeling Shrinkage
横向流量
内部方法
%
0
Modeling Shrinkage
流量
内部方法
%
0
Moisture Absorption
饱和
ASTM D570
%
0
Mechanical Properties
Test Condition
Test Method
Unit
LCP/SUMITOMO JAPAN/E6007LHF
Tensile Strength
ASTM D638
Mpa
1
Tensile Elongation
断裂
ASTM D638
%
5
Flexural Modulus
23°C
ASTM D790
Mpa
1
Flexural Modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
1
Flexural Strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
1
Flexural Strength
23°C
ASTM D790
Mpa
1
Tensile Elongation?(Break)
ASTM D638/ISO 527
%
5
Thermal Properties
Test Condition
Test Method
Unit
LCP/SUMITOMO JAPAN/E6007LHF
Deflection Temperature Under Load?
ASTM D648/ISO 75
℃（℉）
2
Linear thermal expansion coefficient
流动 : 150°C
内部方法
cm/cm/°C
2
Linear thermal expansion coefficient
横向 : 150°C
内部方法
cm/cm/°C
8
Deflection Temperature Under Load?
1.8 MPa, 未退火
ASTM D648
°C
2
Electrical performance
Test Condition
Test Method
Unit
LCP/SUMITOMO JAPAN/E6007LHF
Comparative Tracking Index
IEC 60112
V
1
Arc Resistance
ASTM D495
sec
1
Volume Resistivity
ASTM D257
ohms·cm
1
Impact Properties
Test Condition
Test Method
Unit
LCP/SUMITOMO JAPAN/E6007LHF
Unnotched Izod Impact Strength
6.40 mm
ASTM D256
J/m
2
Flammability
Test Condition
Test Method
Unit
LCP/SUMITOMO JAPAN/E6007LHF
内部方法
°C
3
Oxygen Index
ISO 527-1,-2(JIS K7161,7162)
%
4
Injection
Test Condition
Test Method
Unit
LCP/SUMITOMO JAPAN/E6007LHF
Holding Pressure
Mpa
2
Back Pressure
Mpa
1
Drying Time
hr
4
Drying Temperature
°C
1
Processing (Melt) Temp
°C
3
Rear Temperature
°C
2
Front Temperature
°C
3
Middle Temperature
°C
3
Screw Speed
rpm
5
Mold Temperature
°C
4
Nozzle Temperature
°C
3
Injection Pressure
Mpa
8