ABS/PMMA STAREX® BF-0670 BK22101 Samsung Cheil South Korea
467
- Properties:High temperature resistanAging resistanceHigh impact resistance
- Usages:Electrical appliancesElectronic and electricalAutomotive componentsLighting fixtures
Compare
View PricesTechnical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 220°C/10.0kg | ASTMD1238 | 25 | g/10min |
| 220°C/10.0kg | ISO1133 | 24 | g/10min | |
| Modeling Shrinkage | MD：3.20mm | ASTMD955 | 0.30 | % |
| TD：3.20mm | ASTMD955 | 0.30 | % | |
| TD:3.20mm | ISO2577 | 0.40 | % | |
| MD:3.20mm | ISO2577 | 0.40 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress | 屈服 | ISO527-2/50 | 52.0 | Mpa |
| 断裂 | ISO527-2/50 | 36.0 | Mpa | |
| Tensile Strain | 断裂 | ISO527-2/50 | 22 | % |
| Tensile Modulus | ASTMD638 | 2080 | Mpa | |
| Flexural Modulus | ISO178 | 2360 | Mpa | |
| ASTMD790 | 2350 | Mpa | ||
| Tensile Strength | 断裂 | ASTMD638 | 36.3 | Mpa |
| 屈服 | ASTMD638 | 49.0 | Mpa | |
| Tensile Elongation | 断裂 | ASTMD638 | 18 | % |
| Flexural Strength | ASTMD790 | 66.7 | Mpa | |
| Flexural Stress | ISO178 | 70.0 | Mpa | |
| Tensile Modulus | ISO527-2/50 | 2500 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 1.8MPa,未退火,6.40mm | ASTMD648 | 80.0 | °C |
| 1.8MPa,Unannealed,4.00mm | ISO75-2/A | 72.0 | °C | |
| 1.8MPa,Annealed,4.00mm | ISO75-2/A | 86.0 | °C | |
| 0.45MPa,未退火,6.40mm | ASTMD648 | 90.0 | °C | |
| 0.45MPa,Unannealed,4.00mm | ISO75-2/B | 83.0 | °C | |
| 0.45MPa,Annealed,4.00mm | ISO75-2/B | 92.0 | °C | |
| Vicat Softening Temperature | -- | ISO306/B50 | 92.090.0 | °C |
| -- | ISO306/B120 | 92.0 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Notched Izod Impact Strength | 23°C | ISO180/1A | 7.4 | kJ/m² |
| 23°C | ISO179/1eA | 8.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R级 | ASTMD785 | 114 | |
| R级 | ISO2039-2 | 115 | ||
| Pencil Hardness | --6 | JISK5401 | F | |
| --7 | JISK5401 | F |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL94 | HB | |
| 2.0mm | UL94 | HB | ||
| 3.0mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.