Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD：23°C | ISO294-4 | 0.60到0.80 | % |
| Melt Volume flow Rate | 220°C/10.0kg | ISO1133 | 8.00 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Modulus | 23°C | ISO178 | 2250 | Mpa |
| Flexural Stress | 23°C | ISO178 | 69.0 | Mpa |
| Tensile Stress | 23°C | ISO527-2 | 45.0 | Mpa |
| Charpy Notched Impact Strength | | | 27 | KJ/m |
| Tensile Modulus | 23°C | ISO527-2 | 2200 | Mpa |
| Flexural Modulus | | | 2250 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | | | 80 | °C |
| Deflection Temperature Under Load? | 1.8MPa,未退火 | ISO75-2/Af | 80.0 | °C |
| Flame Rating | | UL94 | HB | |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 9E-05 | cm/cm/°C |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R计秤,23°C | ISO2039-2 | 100 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | | | 8 | CM |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.