Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D792/ISO 1183 | 1.25 | |
| Modeling Shrinkage | | ASTM D955 | MD 0.1～0.4 | % |
| Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.01 | % |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD | 内部方法 | 0.50to0.80 | % |
| Modeling Shrinkage | MD | 内部方法 | 0.10to0.40 | % |
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.010 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | 断裂 | ISO527-2 | 120 | Mpa |
| Tensile Strain | 断裂 | ISO527-2 | 2.1 | % |
| Flexural Stress | | ISO178 | 185 | Mpa |
| Tensile Elongation?(Break) | | ASTM D638/ISO 527 | 2.1 | % |
| Tensile Modulus | | ISO527-2 | 9700 | Mpa |
| Tensile Strength | | ASTM D638/ISO 527 | 120 | kg/cm²(MPa)[Lb/in²] |
| Tensile Elongation | 断裂 | | 2.3 | % |
| Rockwell Hardness | | ASTM D785 | 70 | |
| Flexural Modulus | | ASTM D790/ISO 178 | 9.2 | kg/cm²(MPa)[Lb/in²] |
| Flexural Modulus | | ISO178 | 9200 | Mpa |
| Flexural Strength | | ASTM D790/ISO 178 | 185 | kg/cm²(MPa)[Lb/in²] |
| Flexural Modulus | | | 8100 | Mpa |
| Tensile Strength | | | 165 | Mpa |
| Tensile Strength (Break) | | | 105 | Mpa |
| Izod Impact Strength | 3.2mm 没有Notch | | 40 | KJ/m |
| Izod Impact Strength | 4mm 有Notch | | 10 | KJ/m |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flammability | 1/32英寸 | UL 94 | HB | |
| Linear thermal expansion coefficient | MD：-30到30°C | TMA | 1.8E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | TD：-30to30°C | TMA | 3.9E-05 | cm/cm/°C |
| RTIElec | | UL746 | 50.0 | °C |
| Evolution Calendar intelligent importer | | UL746 | 50.0 | °C |
| RTIStr | | UL746 | 50.0 | °C |
| Burning Rate | | UL94 | HB/0.80 | |
| Deflection Temperature Under Load? | | | 235 | °C |
| Deflection Temperature Under Load? | 0.45MPa,未退火 | ISO75-2/B | 265 | °C |
| Deflection Temperature Under Load? | 1.8MPa,未退火 | ISO75-2/A | 240 | °C |
| Linear expansion coefficient | | ASTM D696/ISO 11359 | MD 1.8 | mm/mm.℃ |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Constant | 1MHz | IEC60250 | 2.90 | |
| Arc Resistance | | ASTMD495 | PLC6 | |
| Arc Resistance | | ASTM D495/IEC 60112 | 120 | |
| Volume Resistivity | | ASTM D257/IEC 60093 | >1.0*10^16 | Ω.cm |
| Volume Resistivity | | IEC60093 | >1.0E+16 | ohms·cm |
| Dissipation Factor? | 1MHz | IEC60250 | <1.0E-3 | |
| Comparative Tracking Index | CTI)3 | IEC60112 | PLC1 | |
| Dielectric Strength | | ASTMD149 | 45 | KV/mm |
| Processing | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD | | 0.35 | % |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod impact strength | 23°C | ISO180 | 36 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179 | 43 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | >0.75mm | UL94 | HB | |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | | | 0.05 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.