SPS XAREC™ C132 IDEMITSU JAPAN

151

Unit Price:
$8050 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:enhance Glass fiber reinforced High temperature resistan
Application Areas:Household goods
Color:--
Grade:--

Technical Data Sheet

Physical Properties	Test Method	Test Result	Unit
Density	ASTM D792/ISO 1183	1.25
Modeling Shrinkage	ASTM D955	MD 0.1～0.4	%
Moisture Absorption 23℃/24H	ASTM D570/ISO 62	0.01	%

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD	内部方法	0.50to0.80	%
Modeling Shrinkage	Modeling Shrinkage	MD	内部方法	0.10to0.40	%
Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.010	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Stress	Break	ISO527-2	120	Mpa
Tensile Strain	Break	ISO527-2	2.1	%
Flexural Stress		ISO178	185	Mpa
Tensile Elongation?(Break)		ASTM D638/ISO 527	2.1	%
Tensile Modulus		ISO527-2	9700	Mpa
Tensile Strength		ASTM D638/ISO 527	120	kg/cm²(MPa)[Lb/in²]
Tensile Elongation	Break		2.3	%
Rockwell Hardness		ASTM D785	70
Flexural Modulus		ASTM D790/ISO 178	9.2	kg/cm²(MPa)[Lb/in²]
Flexural Modulus	Flexural Modulus		ISO178	9200	Mpa
Flexural Strength		ASTM D790/ISO 178	185	kg/cm²(MPa)[Lb/in²]
Flexural Modulus			8100	Mpa
Tensile Strength			165	Mpa
Tensile Strength (Break)			105	Mpa
Izod Impact Strength	3.2mm 没有Notch		40	KJ/m
Izod Impact Strength	Izod Impact Strength	4mm 有Notch		10	KJ/m

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Flammability	1/32英寸	UL 94	HB
Linear thermal expansion coefficient	MD：-30to30°C	TMA	1.8E-05	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD：-30to30°C	TMA	3.9E-05	cm/cm/°C
RTIElec		UL746	50.0	°C
Evolution Calendar intelligent importer		UL746	50.0	°C
RTIStr		UL746	50.0	°C
Burning Rate		UL94	HB/0.80
Deflection Temperature Under Load?			235	°C
	Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	265	°C
	Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	240	°C
Linear expansion coefficient		ASTM D696/ISO 11359	MD 1.8	mm/mm.℃

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Constant	1MHz	IEC60250	2.90
Arc Resistance		ASTMD495	PLC6
Arc Resistance	Arc Resistance		ASTM D495/IEC 60112	120
Volume Resistivity		ASTM D257/IEC 60093	>1.0*10^16	Ω.cm
Volume Resistivity	Volume Resistivity		IEC60093	>1.0E+16	ohms·cm
Dissipation Factor?	1MHz	IEC60250	<1.0E-3
Comparative Tracking Index	CTI)3	IEC60112	PLC1
Dielectric Strength		ASTMD149	45	KV/mm

Processing	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD		0.35	%

Impact Properties	Test Condition	Test Method	Test Result	Unit
Notched Izod impact strength	23°C	ISO180	36	kJ/m²
Charpy Unnotched Impact Strength	23°C	ISO179	43	kJ/m²

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	>0.75mm	UL94	HB

Physical	Test Condition	Test Method	Test Result	Unit
Moisture Absorption			0.05	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.