Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 260℃/2.16Kg | ISO1133 | 32 | cm3/10min |
| Melt Mass-Flow Rate | 190℃/2.16Kg | ISO1133 | 1.8 | g/10min |
| Melt Mass-Flow Rate | 230℃/2.16Kg | ISO1133 | 11 | g/10min |
| Melt Mass-Flow Rate | 水蒸气渗透性 | | 3.70 | gmil/(m2day |
| Melt Mass-Flow Rate | 氧渗透 | | 997 | cm3mil/(m2dayatm |
| Melt Mass-Flow Rate | 水蒸气穿透率 | ISO15106-3 | 0.0008 | g/m²/day |
| Melt Mass-Flow Rate | 厚度 | | 70 | microns |
| Moisture Absorption | (23°C,24hr) | ISO62 | 0.01 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 2.6 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 20 | kJ/m² |
| Tensile Elongation?(Break) | MD,23°C | ISO527-2 | 2.9 | % |
| Tensile Elongation?(Break) | TD,23°C | ISO527-2 | 3 | % |
| Tensile Elongation?(Break) | 23°C | ISO527-2 | 4.5 | % |
| Tensile Modulus | 23°C | ISO527-2 | 2600 | Mpa |
| Tensile Modulus | TD,23°C | ISO527-2 | 1800 | Mpa |
| Tensile Modulus | MD,23°C | ISO527-2 | 2200 | Mpa |
| Tensile Modulus | 断裂拉伸强度 | ISO527-3 | 57 | Mpa |
| Tensile Modulus | 断裂拉伸强度 | ISO527-3 | 50 | Mpa |
| Tensile Modulus | Elmendorf撕裂强度 | ISO6383-2 | 225 | g |
| Tensile Modulus | Elmendorf撕裂强度 | ISO6383-2 | 230 | g |
| Tensile Modulus | 跌落试验 | ISO7765-1 | <=36 | g |
| Tensile Strength | 23°C | ISO527-2 | 63 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45MPa未退火 | ISO75-2/Bf | 75 | °C |
| Vicat Softening Temperature | | ISO306/B50 | 80 | °C |
| Vicat Softening Temperature | 玻璃转化温度 | ISO11357-2 | 78 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation Factor? | 相对漏电起痕指数 | IEC60112 | 600 | V |
| Volume Resistivity | | IEC60093 | 1E+14 | Ω.cm |
| Dielectric Constant | 23°C | IEC60250 | 2.35 | 1kHz |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Refractive index of light | | ISO489 | 1.53 | °C |
| Gloss | | ISO2813 | >=100 | % |
| Haze | | ISO13468-2 | <=0.1 | % |
| Light Transmittance (2000μm) | | ISO13468-2 | 91 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.