Certificates
COC 8007F-04 JAPAN POLYPLASTIC
TOPAS®
LCD application、Optical applications
Dimensional stability、Chemical resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical Properties
Test Condition
Test Method
Unit
COC/JAPAN POLYPLASTIC/8007F-04
Melt Mass-Flow Rate
190℃/2.16Kg
ISO1133
g/10min
1
Melt Mass-Flow Rate
230℃/2.16Kg
ISO1133
g/10min
1
Melt Mass-Flow Rate
水蒸气穿透率
ISO15106-3
g/m²/day
0
Melt Mass-Flow Rate
260℃/2.16Kg
ISO1133
cm3/10min
3
Moisture Absorption
(23°C,24hr)
ISO62
%
0
Mechanical Properties
Test Condition
Test Method
Unit
COC/JAPAN POLYPLASTIC/8007F-04
Tensile Elongation?(Break)
23°C
ISO527-2
%
4
Tensile Elongation?(Break)
MD,23°C
ISO527-2
%
2
Tensile Elongation?(Break)
TD,23°C
ISO527-2
%
3
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
2
Charpy Unnotched Impact Strength
23°C
ISO179/1eU
kJ/m²
2
Tensile Modulus
23°C
ISO527-2
Mpa
2
Tensile Modulus
TD,23°C
ISO527-2
Mpa
1
Tensile Modulus
MD,23°C
ISO527-2
Mpa
2
Tensile Modulus
断裂拉伸强度
ISO527-3
Mpa
5
Tensile Modulus
断裂拉伸强度
ISO527-3
Mpa
5
Tensile Modulus
Elmendorf撕裂强度
ISO6383-2
g
2
Tensile Modulus
Elmendorf撕裂强度
ISO6383-2
g
2
Tensile Modulus
跌落试验
ISO7765-1
g
<
Tensile Strength
23°C
ISO527-2
Mpa
6
Thermal Properties
Test Condition
Test Method
Unit
COC/JAPAN POLYPLASTIC/8007F-04
Deflection Temperature Under Load?
0.45MPa未退火
ISO75-2/Bf
°C
7
Vicat Softening Temperature
ISO306/B50
°C
8
Vicat Softening Temperature
玻璃转化温度
ISO11357-2
°C
7
Electrical performance
Test Condition
Test Method
Unit
COC/JAPAN POLYPLASTIC/8007F-04
Dissipation Factor?
相对漏电起痕指数
IEC60112
V
6
Dielectric Constant
23°C
IEC60250
1kHz
2
Volume Resistivity
IEC60093
Ω.cm
1
optical performance
Test Condition
Test Method
Unit
COC/JAPAN POLYPLASTIC/8007F-04
Gloss
ISO2813
%
>
Light Transmittance (2000μm)
ISO13468-2
%
9
Haze
ISO13468-2
%
<
Refractive index of light
ISO489
°C
1