Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 饱和,23°C | ISO62 | 0.50 | % |
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.20 | % |
| Apparent Density | | ISO60 | 0.70 | g/cm³ |
| Melt Volume flow Rate | 260°C/5.0kg | ISO1133 | 16.0 | cm3/10min |
| Density / Specific Gravity | 23°C | ISO1183 | 1.20 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Nominal Tensile Strain at Break | 23°C | ISO527-2/50 | >50 | % |
| Tensile Stress | 屈服,23°C | ISO527-2/50 | 50.0 | Mpa |
| Tensile Stress | 断裂,23°C | ISO527-2/50 | 45.0 | Mpa |
| Tensile Strain | 屈服,23°C | ISO527-2/50 | 4.0 | % |
| Tensile Modulus | 23°C | ISO527-2/1 | 2150 | Mpa |
| Flexural Modulus | 23°C | ISO178 | 2100 | Mpa |
| Flexural Stress | 23°C | ISO178 | 75.0 | Mpa |
| Flexural Stress | 3.5%Strain,23°C | ISO178 | 66.0 | Mpa |
| Flexural Strain | 23°C | ISO178 | 5.5 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| 23°C | ISO8302 | 0.20 | W/m/K |
| Linear thermal expansion coefficient | MD：23到55°C | ISO11359-2 | 9E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | TD：23to55°C | ISO11359-2 | 9E-05 | cm/cm/°C |
| Deflection Temperature Under Load? | 0.45MPa,未退火 | ISO75-2/B | 106 | °C |
| Deflection Temperature Under Load? | 1.8MPa,未退火 | ISO75-2/A | 82.0 | °C |
| Vicat Softening Temperature | | ISO306/B120 | 125 | °C |
| Melting Temperature | | ISO11357-3 | 223 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Relative Permittivity | 23°C,100Hz | IEC60250 | 3.20 | |
| Relative Permittivity | 23°C,1MHz | IEC60250 | 3.10 | |
| Comparative Tracking Index | 解决方案A | IEC60112 | 500 | V |
| Comparative Tracking Index | 解决方案B | IEC60112 | 100 | V |
| Surface Resistivity | | IEC60093 | >1.0E+17 | ohms |
| Volume Resistivity | 23°C | IEC60093 | >1.0E+17 | ohms·cm |
| Dissipation Factor? | 23°C,100Hz | IEC60250 | 1.5E-03 | |
| Dissipation Factor? | 23°C,1MHz | IEC60250 | 0.013 | |
| Dielectric Strength | 23°C,1.00mm | IEC60243-1 | 35 | KV/mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod impact strength | -30°C | ISO180 | NoBreak | |
| Notched Izod impact strength | 23°C | ISO180 | NoBreak | |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak | |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | NoBreak | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 45 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 60 | kJ/m² |
| Notched Izod Impact Strength | -30°C | ISO180/A | 45 | kJ/m² |
| Notched Izod Impact Strength | -20°C | ISO180/A | 52 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/A | 60 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball Indentation Hardness | | ISO2039-1 | 100 | Mpa |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | 1.6mm | UL94 | HB | |
| Glow Wire Flammability Index | 2.0mm | IEC60695-2-12 | 700 | °C |
| FMVSS Flammability | >1.00mm | ISO3795 | passed | |
| Oxygen Index | | ISO4589-2 | 21 | % |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|
| 260°C | 内部方法 | 670 | Pa·s |
| ElectrolyticalCorrosion | 23°C | IEC60426 | A1 | |
| ISO Shortname | | | ISO7792-1-PBT/PC,MHPR,-020 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.