PC/PBT Makroblend® KU2-7912/4 BK COVESTRO GERMANY

135

Unit Price:
$3565 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
16MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:wear resistant High elasticity Fast forming cycle
Application Areas:film Casters shoes
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	Saturation,23°C	ISO62	0.50	%
Moisture Absorption	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.20	%
Apparent Density		ISO60	0.70	g/cm³
Melt Volume flow Rate	260°C/5.0kg	ISO1133	16.0	cm3/10min
Density / Specific Gravity	23°C	ISO1183	1.20	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Nominal Tensile Strain at Break	23°C	ISO527-2/50	>50	%
Tensile Stress	Yield,23°C	ISO527-2/50	50.0	Mpa
Tensile Stress	Tensile Stress	Break,23°C	ISO527-2/50	45.0	Mpa
Tensile Strain	Yield,23°C	ISO527-2/50	4.0	%
Tensile Modulus	23°C	ISO527-2/1	2150	Mpa
Flexural Modulus	23°C	ISO178	2100	Mpa
Flexural Stress	23°C	ISO178	75.0	Mpa
Flexural Stress	Flexural Stress	3.5%Strain,23°C	ISO178	66.0	Mpa
Flexural Strain	23°C	ISO178	5.5	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
ThermalConductivity5	23°C	ISO8302	0.20	W/m/K
Linear thermal expansion coefficient	MD：23to55°C	ISO11359-2	9E-05	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD：23to55°C	ISO11359-2	9E-05	cm/cm/°C
Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	106	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	82.0	°C
Vicat Softening Temperature		ISO306/B120	125	°C
Melting Temperature		ISO11357-3	223	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Relative Permittivity	23°C,100Hz	IEC60250	3.20
Relative Permittivity	Relative Permittivity	23°C,1MHz	IEC60250	3.10
Comparative Tracking Index	SolutionA	IEC60112	500	V
Comparative Tracking Index	Comparative Tracking Index	SolutionB	IEC60112	100	V
Surface Resistivity		IEC60093	>1.0E+17	ohms
Volume Resistivity	23°C	IEC60093	>1.0E+17	ohms·cm
Dissipation Factor?	23°C,100Hz	IEC60250	1.5E-03
Dissipation Factor?	Dissipation Factor?	23°C,1MHz	IEC60250	0.013
Dielectric Strength	23°C,1.00mm	IEC60243-1	35	KV/mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Notched Izod impact strength	-30°C	ISO180	NoBreak
Notched Izod impact strength	Notched Izod impact strength	23°C	ISO180	NoBreak
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	NoBreak
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	NoBreak
Charpy Notched Impact Strength	-30°C	ISO179/1eA	45	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	60	kJ/m²
Notched Izod Impact Strength	23°C	ISO180/A	60	kJ/m²
	Notched Izod Impact Strength	-30°C	ISO180/A	45	kJ/m²
	Notched Izod Impact Strength	Notched Izod Impact Strength	-20°C	ISO180/A	52	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Ball Indentation Hardness		ISO2039-1	100	Mpa

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	1.6mm	UL94	HB
Glow Wire Flammability Index	2.0mm	IEC60695-2-12	700	°C
FMVSS Flammability	>1.00mm	ISO3795	passed
Oxygen Index		ISO4589-2	21	%

Supplementary information	Test Condition	Test Method	Test Result	Unit
GottfertMeltViscosity7	260°C	内部方法	670	Pa·s
ElectrolyticalCorrosion	23°C	IEC60426	A1
ISO Shortname			ISO7792-1-PBT/PC,MHPR,-020

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.