| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | 流动 | ASTM D955 | 0.22 | % |
| Modeling Shrinkage | 横向流动 | ASTM D955 | 0.66 | % |
| Moisture Absorption | 饱和 | ASTM D570 | 0.020 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Elongation | 断裂 | ASTM D638 | 4.3 | % |
| Flexural Modulus | 23°C | ASTM D790 | 13500 | Mpa |
| Flexural Strength | 23°C | ASTM D790 | 134 | Mpa |
| Shearing Strength | | ASTM D732 | 50.0 | Mpa |
| Poisson Ratio | | ASTM E132 | 0.39 | |
| Tensile Strength | | ASTM D638 | 126 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear thermal expansion coefficient | 流动 : 50 到 150°C | ASTM D696 | 1.1E-5 | cm/cm/°C |
| Linear thermal expansion coefficient | 横向 : 50 到 150°C | ASTM D696 | 6.5E-5 | cm/cm/°C |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火 | ASTM D648 | 284 | °C |
| RTI | 3.2 mm | UL 746 | 240 | °C |
| RTI Imp | 3.2 mm | UL 746 | 200 | °C |
| RTI Elec | 3.2 mm | UL 746 | 220 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Constant | 1 kHz | ASTM D150 | 4.30 | |
| Dielectric Constant | 1 MHz | ASTM D150 | 3.90 | |
| Arc Resistance | | ASTM D495 | 130 | sec |
| Volume Resistivity | | ASTM D257 | 1.0E+15 | ohms·cm |
| Dissipation Factor? | 1 kHz | ASTM D150 | 0.019 | |
| Dissipation Factor? | 1 MHz | ASTM D150 | 0.028 | |
| Comparative Tracking Index | | UL 746 | 165 | V |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|
| Injection Pressure | | | 78.0 到 157 | Mpa |
| Suggested Max Regrind | | | 30 | % |
| Injection Rate | | | 中等偏快 | |
| Drying Time | | | 3.0 | hr |
| Rear Temperature | | | 300 到 320 | °C |
| Middle Temperature | | | 320 到 350 | °C |
| Front Temperature | | | 340 到 370 | °C |
| Nozzle Temperature | | | 340 到 370 | °C |
| Back Pressure | | | 0.980 到 4.90 | Mpa |
| Screw Speed | | | 50 到 100 | rpm |
| Drying Temperature | | | 120 到 150 | °C |
| Mold Temperature | | | 70 到 160 | °C |
| Holding Pressure | | | 20.0 到 39.0 | Mpa |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Unnotched Izod Impact Strength | 6.40 mm | ASTM D256 | 280 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R 级 | ASTM D785 | 103 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Oxygen Index | | ASTM D2863 | 46 | % |
| Flame Rating | 0.30 mm | UL 94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.