Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | 流动 | ISO 294 | 2 | % |
| Modeling Shrinkage | 垂直 | ISO 294 | 2 | % |
| Moisture Absorption | | ISO 62 | 0.03 | % |
| Moisture Absorption | | ASTM D570 | 0.01-0.03 | % |
| Melt index | 230°C 3.8kg | ASTM D1238 | 5-26.5 | g/10min |
| Melt Viscosity | 230℃100s | ASTM D3835 | 6~12 | kPoise |
| Moisture Absorption | | ISO 62 | 0.015 | % |
| proportion | | ISO 1183 | 1780 | kg/㎥ |
| proportion | 23℃ | ASTM D792 | 1.77-1.79 | g/㎤ |
| Melt Mass-Flow Rate | 230℃ 5kg | ISO 1133 | 10 | ㎤/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod Impact Strength | 23℃ | ASTM D256 | 0.0801-0.214 | KJ/m |
| Charpy Unnotched Impact Strength | 23℃ | ISO 179 | 208 | kJ/㎡ |
| Charpy Unnotched Impact Strength | -30℃ | ISO 179 | 189 | kJ/㎡ |
| 23℃ | ASTM D695 | 68.9~103 | Mpa |
| Unnotched Izod Impact Strength | 23℃ | ASTM D256 | 1.07-4.27 | KJ/m |
| Taber Abrasion Resistance | CS-17轮1kg | ASTM G195 | 5~9 | mg/1000cy |
| Coefficient of Friction | 静态 对钢23℃ | ASTM D1894 | 0.2 | |
| Coefficient of Friction | 静态 对钢23℃ | ASTM D1894 | 0.14 | |
| Charpy Notched Impact Strength | 23℃ | ISO 179 | 8 | kJ/㎡ |
| Charpy Notched Impact Strength | -30°C | ISO 179 | 5 | kJ/㎡ |
| Tensile Modulus | | ISO 527 | 2200 | Mpa |
| Tensile Modulus | 23℃ | ASTM D638 | 1380-2310 | Mpa |
| Tensile Strength | 屈服 | ISO 527 | 54 | Mpa |
| Tensile Strength | 屈服23℃ | ASTM D638 | 44.8-55.2 | Mpa |
| Tensile Strength | 断裂23℃ | ASTM D638 | 34.5-55.2 | Mpa |
| Tensile Elongation | 屈服 | ISO 527 | 8 | % |
| Tensile Elongation | 屈服23℃ | ASTM D638 | 570 | % |
| Tensile Elongation | 断裂 | ISO 527 | 50 | % |
| Tensile Elongation | 断裂23℃ | ASTM D638 | 20-100 | % |
| Flexural Modulus | 23℃ | ASTM D790 | 1380-2310 | Mpa |
| Flexural Strength | 23℃5.0%应变 | ASTM D790 | 58.6-75.8 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8MPa | ISO 75 | 110 | °C |
| Deflection Temperature Under Load? | 1.8MPa120℃/hr | ASTM D648 | 105-115 | °C |
| Deflection Temperature Under Load? | 0.45MPa | ISO 75 | 132 | °C |
| Deflection Temperature Under Load? | 0.45MPa120℃/hr | ASTM D648 | 125-140 | °C |
| Vicat Softening Temperature | 50℃/hr 50N | ISO 306 | 139 | °C |
| Thermal Conductivity | | ASTM E1461 | 0.17-0.19 | W/(m.K) |
| Melting temperature | 10℃/min | ISO 11357 | 168 | °C |
| Melting temperature | | ASTM D3418 | 165-172 | °C |
| Glass Transition Temperature | 10℃/min | ISO 11357 | -40 | °C |
| Glass Transition Temperature | | ASTM D7028 | -40.6-38.3 | °C |
| Coefficient of Linear Thermal Expansion | 流动 | ISO 11359 | 0.00015 | m/m/k |
| Coefficient of Linear Thermal Expansion | 23℃ | ASTM D696 | 1.19E-3~1.44E-3 | cm/cm/℃ |
| Specific Heat | | 内部测试方法 | 745-958 | J/(kg.k) |
| TGA在空气中1 %质量损失 | 内部测试方法 | 375 | °C |
| TGA在通气中1%质量损失 | 内部测试方法 | 410 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume Resistivity | | IEC 60093 | 2000000000000 | Ω.m |
| CTI | | IEC 60112 | 600 | V |
| Insulation strength | | IEC 60243 | 21 | KV/mm |
| Insulation strength | 23℃ | ASTM D149 | 1.7 | KV/mm |
| Volume Resistivity | 20℃ 65RH | ASTM D257 | 200000000000000 | Ω.cm |
| Surface resistance | | IEC 60093 | 1000000000000000 | Ω |
| Dissipation Factor? | 100Hz | IEC 60250 | 0.032 | |
| Dissipation Factor? | 1MHz | IEC 60250 | 0.214 | |
| Dissipation Factor? | 100kHz | ASTM D150 | 0.01-0.21 | |
| Dielectric Constant | 100Hz | IEC 60250 | 9 | |
| Dielectric Constant | 1MHz | IEC 60250 | 7 | |
| Dielectric Constant | iKHz | ASTM D150 | 4.5-9.5 | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness (Shore D) | 23℃ | ASTM D2240 | 76~80 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Refractive index of light | 钠光谱D线 | ASTM D542 | 1.42 | |
| Flame Rating | Test Condition | Test Method | Test Result | Unit |
|---|
| Fire rating | 本色1.5mm | UL94 | V-0 | |
| Oxygen Index | | ISO 4589 | 43 | % |
| Oxygen Index | | ASTM D2863 | 44 | % |
| Test Condition | Test Method | Test Result | Unit |
|---|
| Fire rating | 本色1.5mm | UL94 | V-0 | |
| RTI Elec | 本色 1.5mm | UL 746B | 150 | °C |
| RTI Imp | 本色 1.5mm | UL746B | 150 | °C |
| RTI Str | 本色 1.5mm | UL 746B | 150 | °C |
| Outdoor Suitability | | UL-746C | f1 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.