PVDF Kynar® 720 ARKEMA CHANGSHU
217
- Unit Price:
- $12269 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Flow | ISO 294 | 2 | % |
| 垂直 | ISO 294 | 2 | % | |
| Water absorption rate | ISO 62 | 0.03 | % | |
| ASTM D570 | 0.01-0.03 | % | ||
| Melt index | 230°C 3.8kg | ASTM D1238 | 5-26.5 | g/10min |
| Melt viscosity | 230℃100s | ASTM D3835 | 6~12 | kPoise |
| Moisture absorption rate | ISO 62 | 0.015 | % | |
| proportion | ISO 1183 | 1780 | kg/㎥ | |
| 23℃ | ASTM D792 | 1.77-1.79 | g/㎤ | |
| Yirong Index | 230℃ 5kg | ISO 1133 | 10 | ㎤/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Cantilever beam gap impact | 23℃ | ASTM D256 | 0.0801-0.214 | KJ/m |
| Simple supported beam without notch impact | 23℃ | ISO 179 | 208 | kJ/㎡ |
| -30℃ | ISO 179 | 189 | kJ/㎡ | |
| Compression slip | 23℃ | ASTM D695 | 68.9~103 | Mpa |
| Cantilever beam without notch impact | 23℃ | ASTM D256 | 1.07-4.27 | KJ/m |
| Tiber wear and tear | CS-17轮1kg | ASTM G195 | 5~9 | mg/1000cy |
| friction coefficient | 静态 对钢23℃ | ASTM D1894 | 0.2 | |
| 静态 对钢23℃ | ASTM D1894 | 0.14 | ||
| Impact of simply supported beam gap | 23℃ | ISO 179 | 8 | kJ/㎡ |
| -30°C | ISO 179 | 5 | kJ/㎡ | |
| Tensile modulus | ISO 527 | 2200 | Mpa | |
| 23℃ | ASTM D638 | 1380-2310 | Mpa | |
| tensile strength | Yield | ISO 527 | 54 | Mpa |
| Yield23℃ | ASTM D638 | 44.8-55.2 | Mpa | |
| Break23℃ | ASTM D638 | 34.5-55.2 | Mpa | |
| elongation | Yield | ISO 527 | 8 | % |
| Yield23℃ | ASTM D638 | 570 | % | |
| Break | ISO 527 | 50 | % | |
| Break23℃ | ASTM D638 | 20-100 | % | |
| Bending modulus | 23℃ | ASTM D790 | 1380-2310 | Mpa |
| bending strength | 23℃5.0%Strain | ASTM D790 | 58.6-75.8 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa | ISO 75 | 110 | °C |
| 1.8MPa120℃/hr | ASTM D648 | 105-115 | °C | |
| 0.45MPa | ISO 75 | 132 | °C | |
| 0.45MPa120℃/hr | ASTM D648 | 125-140 | °C | |
| Vicat softening temperature | 50℃/hr 50N | ISO 306 | 139 | °C |
| thermal conductivity | ASTM E1461 | 0.17-0.19 | W/(m.K) | |
| Melting temperature | 10℃/min | ISO 11357 | 168 | °C |
| ASTM D3418 | 165-172 | °C | ||
| Glass transition temperature | 10℃/min | ISO 11357 | -40 | °C |
| ASTM D7028 | -40.6-38.3 | °C | ||
| Coefficient of linear expansion | Flow | ISO 11359 | 0.00015 | m/m/k |
| 23℃ | ASTM D696 | 1.19E-3~1.44E-3 | cm/cm/℃ | |
| Specific heat capacity | 内部测试方法 | 745-958 | J/(kg.k) | |
| decomposition temperature | TGA在空气中1 %质量损失 | 内部测试方法 | 375 | °C |
| TGA在通气中1%质量损失 | 内部测试方法 | 410 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Accumulation resistor | IEC 60093 | 2000000000000 | Ω.m | |
| CTI | IEC 60112 | 600 | V | |
| Insulation strength | IEC 60243 | 21 | KV/mm | |
| 23℃ | ASTM D149 | 1.7 | KV/mm | |
| Volume resistance | 20℃ 65RH | ASTM D257 | 200000000000000 | Ω.cm |
| Surface resistance | IEC 60093 | 1000000000000000 | Ω | |
| Dissipation factor | 100Hz | IEC 60250 | 0.032 | |
| 1MHz | IEC 60250 | 0.214 | ||
| 100kHz | ASTM D150 | 0.01-0.21 | ||
| Dielectric constant | 100Hz | IEC 60250 | 9 | |
| 1MHz | IEC 60250 | 7 | ||
| iKHz | ASTM D150 | 4.5-9.5 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore hardness D | 23℃ | ASTM D2240 | 76~80 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index | 钠光谱D线 | ASTM D542 | 1.42 |
| Flame retardant performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Fire rating | 本色1.5mm | UL94 | V-0 | |
| Extreme Oxygen Index | ISO 4589 | 43 | % | |
| ASTM D2863 | 44 | % |
| UL | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Fire rating | 本色1.5mm | UL94 | V-0 | |
| RTI Elec | 本色 1.5mm | UL 746B | 150 | °C |
| RTI Imp | 本色 1.5mm | UL746B | 150 | °C |
| RTI Str | 本色 1.5mm | UL 746B | 150 | °C |
| Outdoor applicability | UL-746C | f1 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.